Effect of Thermomechanical Controlled Processing on the Microstructure and Mechanical Properties of Fe-C-Mn-Si Multiphase Steels
スポンサーリンク
概要
- 論文の詳細を見る
In this paper, a three step cooling (first water cooling, subsequent air cooling and second water cooling stage) pattern on the runout table (ROT) was conducted in a laboratory hot rolling mill, and effect of thermomechanical controlled processing (TMCP) on the microstructure and mechanical properties of Fe–C–Mn–Si multiphase steels was investigated. The results showed that the microstructure containing polygonal ferrite, granular bainite and a significant amount of the stable retained austenite can be obtained through three step cooling on the ROT after hot rolling. The first water cooling stage made high density dislocation remain in the austenite, the second water cooling stage avoided pearlite formation, and it is necessary to hold about 10 s during intermediate air cooling on the ROT, which contributes to enhancement the stability of retained austenite. Excellent mechanical properties were obtained through TMCP due to the transformation of retained austenite into martensite during straining (transformation induced plasticity) for the present Fe–C–Mn–Si multiphase steels, and the specimen 3 shows the highest value of total elongation (37%) and the balance of strength and ductility (30 488 MPa%).
- 社団法人 日本鉄鋼協会の論文
- 2006-07-15
著者
-
WU Di
State Street Corporation
-
Li Zhuang
State Key Laboratory Of Electroanalytical Chemistry Changchun Institute Of Applied Chemistry Graduat
-
Li Zhuang
State Key Laboratory Of Electroanalytical Chemistry Changchun Institute Of Applied Chemistry Chinese
-
Li Zhuang
State Key Laboratory Of Rolling And Automation Northeastern University
-
Wu Di
State Key Laboratory Of Rolling And Automation Northeastern University
関連論文
- Inconsistency Resolution Method for RBAC Based Interoperation
- Security Violation Detection for RBAC Based Interoperation in Distributed Environment
- Inconsistency Resolution Method for RBAC Based Interoperation
- Effect of Thermomechanical Controlled Processing on the Microstructure and Mechanical Properties of Fe-C-Mn-Si Multiphase Steels
- Effects of Hot Deformation and Subsequent Austempering on the Mechanical Properties of Si-Mn TRIP Steels
- DNA Network Structures on Various Solid Substrates Investigated by Atomic Force Microscopy
- Preparation of Pt Nanoparticles Assembled in Multilayer Films
- Controlled Organization of Silver Nanoparticles into Network Assemblies by Tuning pH Values
- Self-assembled Gold Nanoparticle Chains in Presence of Silver Ions
- SD2011 Conference Report