The Influence of Reheating Temperature and Direct-cooling Rate after Forging on Microstructure and Mechanical Properties of V-microalloyed Steel 38MnSiVS5

スポンサーリンク

概要

• 論文の詳細を見る

• Wiht the aim of replacing quenched and tempered forging parts and reducing by this way costly and time consuming operations; an industrial forging procedure was developed to evaluate the influence of thermomechanical processing parameters on the microstructure and mechanical properties of vanadium microalloyed steel. In order to study the influence of reheating temperature, after determining the dissolving temperature of vanadium carbonitrides precipitates, samples were heating in temperature rang 1000 to 1200°C. After austenitization at 1100°C, the microalloyed steel billets were forged in a hydraulic press and then cooled with different cooling rates. The metallography and mechanical testing results indicated that by increasing the reheating temperature, the strength and toughness of V-microalloyed steel have not change significantly and so the temperature of 1200°C was selected for forging. By increasing cooling rate, both strength and toughness improve.

• 社団法人 日本鉄鋼協会の論文
• 2006-01-15

著者

• Dini Ghasem

  Department Of Materials Science And Engineering Isfahan University Of Technology

• Vaghefi Mahmood

  Department Of Materials Science And Engineering Isfahan University Of Technology

• SHAFYEI Ali

  Department of Materials Science and Engineering, Isfahan University of Technology

• Shafyei Ali

  Department Of Materials Science And Engineering Isfahan University Of Technology

関連論文

• The Influence of Reheating Temperature and Direct-cooling Rate after Forging on Microstructure and Mechanical Properties of V-microalloyed Steel 38MnSiVS5

スポンサーリンク