• Photo-curable organoborosilicate glasses were synthesized through a catalyst- and solvent-free and non-aqueous alcohol condensation process at low temperature below 100°C. Formation of Si-O-B linkage was confirmed by IR spectra. After irradiation of UV-light, we have successfully cured the prepolymer coatings into prepared transparent and homogeneous thin film. A refractive index of the thin film of B(OH)3: 3-Methacryloxypropyltrimethoxysilane=1:1 composition was measured by a prism coupling method n=1.515 at 633 nm. Moreover, pencil hardnesses according to JIS5400 of photo-cured thin film before and after heat treatment at 550°C were 6H and over 10H, respectively. We demonstrated fabrication of microstructures on transparent thin film by embossing process followed by photo curing.

• 2010-07-15

著者

• 高橋 雅英

  大阪府立大学大学院工学研究科

• 高橋 雅英

  大阪府立大学大学院工学研究科・物質化学専攻・マテリアル工学分野

• 井原 梨恵

  大阪府立大学大学院工学研究科・物質化学専攻・マテリアル工学分野

• 高橋 雅英

  大阪府立大学

関連論文

• 交互共重合型の有機修飾酸化物を用いた光機能性開拓
• 光硬化性ホウケイ酸塩系薄膜材料の作製と微細構造形成
• チタニア-ポリマーハイブリッド薄膜における光誘起微細しわ構造の形成と湿度応答性
• チタニア系ハイブリッド材料を用いた高屈折率変調を有する逆オパール膜の作製
• 612 高効率イオン交換反応の実現に向けたバルク型マクロ多孔性層状腹水酸化物の作製(セラミック/ナノ材料の創製,セラミック/ナノ材料の創成と評価,オーガナイスドセッション8)

スポンサーリンク