• Photoluminescence (PL) of YPO4:Mn2+ codoped with four tetravalent cations (Zr4+, Sn4+, Ti4+, and Si4+) has been investigated at room temperature under excitation with vacuum ultraviolet (VUV) photons at 147 nm. The wavelength is located at the fundamantal absorption edge of YPO4. The concentration of all the cations was set to be 1.0 mol% in preparation. The PL spectra exhibited a blue-green (BG) band peaking at 482 nm. The PL intensity of the BG band is highest when Zr4+ ions were codoped into YPO4:Mn2+, and thus Zr4+-codoping is the best choice for PL enhancement in YPO4:Mn2+ phosphors. It was found that the PL intensity of Zr4+ doped YPO4:Mn2+ reached 80% of that of a well-known VUV phosphor BaMgAl10O17:Eu2+, unless the concentration of Mn2+ and Zr4+ ions was not optimaized.

• 2009-10-01

著者

• 北浦 守

  福井工業高等専門学校 一般科目

関連論文

• 4価金属イオンを共賦活したYPO_4:Mn^蛍光体における発光の特性改善
• その他の関連分野-3 マンガンイオンとジルコニウムイオンを添加したリン酸イットリウムにおける発光特性の改善
• 19pPSB-45 SrAl_2O_4:Eu,Dyにおける光誘起電子スピン共鳴(ポスターセッション,領域5,光物性)
• 25aPS-46 SrAl_2O_4:Eu,Dyにおける長残光の励起過程II(25aPS 領域5ポスターセッション,領域5(光物性))
• 28aPS-39 SrAl_2O_4:EuおよびSrAl_2O_4:Eu,Ln(Ln=Dy,Gd,La)における長残光の励起過程(28aPS 領域5ポスターセッション,領域5(光物性))
• 福井県における融雪地すべりの挙動と観測
• 融雪水による粘土層生成

スポンサーリンク