概要
- 論文の詳細を見る
The crystallographic and magnetic properties of porous NixZn1-xFe2O4 (x = 0.1, 0.5 and 0.9) from wood templates were investigated in this study. The nitrates aqueous precursor solution was infiltrated into the wood specimen at 60°C to retain the original shape and the microstructure of wood. The sintered bodies contained elongated pores enclosed by a thin layer of wall with the thickness about 1-2 μm. The grain size of polycrystalline ferrite was observed to be in the range of 1-1.5 μm. Each grain was horizontally connected to form polycrystalline walls of single-layered grains. The VSM measurement showed that there is an obvious difference of magnetic properties in the parallel and perpendicular direction due to the anisotropic structure of wood template. The coercivity perpendicular to the pores orientation was larger compared to the coercivity parallel to the pores orientation. It is also discovered that the optimum saturation magnetization was achieved at x = 0.5.
- 公益社団法人 日本セラミックス協会の論文
- 2009-09-01
著者
-
Adachi Nobuyasu
Ceramic Research Laboratory Nagoya Institute Of Technology
-
Sia Chee
Ceramic Research Laboratory Nagoya Institute Of Technology
-
Ota Toshitaka
Ceramic Res. Lab. Nagoya Inst. Of Technol.
-
Sasaki Yuji
Ceramic Research Laboratory Nagoya Institute Of Technology
関連論文
- Liquid Phase Epitaxial Growth of (Bi, Lu)_3(Fe, Ga)_5O_ Films with In-Plane Anisotropy for Magneto-Optical Imaging
- Preparation of fine mullite powders with high surface area by agglomeration control of alkoxide-derived precursor sol
- Homogeneous precipitation of alumina precursors via enzymatic decomposition of urea
- Fabrication of transition temperature controlled W-doped VO2 nano particles by aqueous solution
- Growth and Characterization of Functionally Graded Tryglycine Sulphate–Phosphoric Acid Substituted Tryglycine Sulphate Crystals Produced by Solution-Dropping Method
- Thermal, mechanical and chemical properties of sintered monazite-(La, Ce, Nd or Sm)
- Synthesis and thermal reactions of rhabdophane-(Y)
- Leakage Current Properties of Cation-Substituted BiFeO3 Ceramics
- The magnetic properties of porous Ni-Zn ferrites prepared from wood templates
- Porous Ceramics Prepared by Bio-Casting
- Arraying needle-like TiO_2 particles in a composite film by applying ac bias and its transmittance anisotropy
- Fabrication of Photochromic Tungsten Oxide Based Composite Film Using Peroxoisopolytungstic Acid
- Variation of the strain waveform developed in strengthened porcelain upon impact
- Fabrication of WO_3-Based Composite Films and Improvement Its Photochromic Properties by Copper Doping
- Thermal Expansion of NaZr2(PO4)3 Family Ceramics in a Low-Temperature Range