フォトリソグラフィとアノード酸化を利用したAl薄膜の表面加工
スポンサーリンク
概要
- 論文の詳細を見る
This paper addresses a new method of surface patterning for thin aluminum films using photolithography, anodization, and chemical etching. Aluminum film with a thickness of about 150nm was deposited on titanium-coated silicon or slide glass substrates. Subsequently, square masks were patterned on the aluminum film using photolithography. While aluminum film was anodized in 1vol% sulfuric acid, an anodic oxide film formed in the photoresist/aluminum film interface in addition to on open surface regions. In this process, the thickness of the anodic oxide film formed under the photoresist was affected by the bath voltage and the thickness of the titanium layer. Since the thickness of the anodic oxide at open surface regions and at masked regions differed, a patterned surface was developed. In order to examine the surface morphology, the anodic oxide film was removed by chemical etching in 21vol% phosphoric acid. As result, the anodic oxide film was removed, leaving an aluminum film of convex shape on the substrate.
- 一般社団法人 表面技術協会の論文
- 2008-05-01
著者
関連論文
- 3次元立体アルミニウムマスクを用いた石英ガラスの反応性イオンエッチング加工
- 高周波イオンプレーティングによる金-銅合金薄膜の形成
- 411 銅合金ろうによるアルミニウム合金の真空ろう付
- 3次元立体アルミニウムマスクを用いた石英ガラスの反応性イオンエッチング加工
- 441 窒化ケイ素の活性金属ろう付界面における侵食現象
- フォトリソグラフィとアノード酸化を利用したAl薄膜の表面加工
- 表面波による重ね合せ接着継手のき裂進展評価
- 409 Ag-Cu-Ti系ろうによるルビーの侵食現象
- 3次元立体アルミニウムマスクを用いたシリコン基板の反応性イオンエッチング加工
- フォトリソグラフィ-陽極酸化-化学エッチングによるアルミニウム圧延板の装飾的表面加工