タングステン酸塩を用いたクロメート代替化成皮膜の膜形成に及ぼす浴添加剤の効果と膜の組成分析
スポンサーリンク
概要
- 論文の詳細を見る
The chromate alternative conversion coatings were formed on zinc plated steel by immersing it into a chemical conversion bath containing sodium tungstate and phosphoric acid at room temperature. The effects of additives in the bath, such as inorganic and organic acids, on the properties of the coatings were investigated. As a result, it was found that the addition of sulfuric acid made the corrosion resistance of the coatings remarkably improve and that the further addition of borate made the surface of the coatings smooth, fine, and glossy. The bath compositions determined as optimum for both corrosion resistance and the surface appearance of the coatings were 15.0g of Na2WO4·2H2O, 44mL of 85%H3PO4, 2.1mL of H2SO4, and 8.51-26.7g of Na2B4O7·10H2O dissolved in 400mL of water. Also, the optimum pH range of the bath turned out to be 0.9-1.1. The corrosion resistance of the coating was evaluated by the neutral salt spray test, on which the first appearance time of white corrosion products on the surface of the coating was improved to 160-170h, indicating comparatively higher corrosion resistance, suitable as an alternative to chromate conversion coatings formed on zinc plating. The coatings were also examined by glow discharge optical emission spectroscopy and X-ray photoelectron spectroscopy. Their thicknesses were found to be around 0.5μm. It was suggested that the coatings were composed of zinc ions eluted from the zinc plating, tungstate ions consisting of W6+, W5+, and W4+, and phosphate ions.
- 2008-02-01
著者
関連論文
- ケラチン修飾シリカ充填剤の光学分割能と修飾形態
- 固-液共存状態を利用してSPS成形したダイヤモンド粒子分散型Al基複合材料の熱伝導率
- ヒノキ材から調整した多孔性炭素の物性 : 900℃における炭化時間の影響
- タングステン酸塩を用いたクロメート代替化成皮膜の膜形成に及ぼす浴添加剤の効果と膜の組成分析
- 新しいプラスチックめっきプロセス