Influence of sintering atmosphere on the corrosion behavior of the type 410 stainless steel prepared by MIM process (特集 自動車用焼結部品の更なる拡大)

スポンサーリンク

概要

• 論文の詳細を見る

• The mixtures of Type 410 stainless steel powder and the binder were injected into dumbbell type tensile test bars, and the green compacts thus obtained were subjected to pre-sintering at 873 K for 7.2 ks in the vacuum with various degrees of 0.1, 4 and 133 Pa followed by sintering at 1623 K for 7.2 ks under Ar gas flowing in the same vacuum of 0.1, 4 and 133 Pa. The Type 410 specimens sintered in vacuum of 0.1, 4, and 133 Pa were designated as Specimen 1, 2 and 3, respectively. In addition, the Type 410 specimen pre-sintered at 873 K for 7.2 ks in H2 gas and sintered at 1623 K for 7.2 ks under Ar gas flowing in the same vacuum of 0.1 Pa was also prepared. It was referred to as Specimen 1 A. By using these four specimens mentioned above, the influence of sintering atmosphere on the corrosion behavior of the Type 410 stainless steel specimen prepared by MIM process was studied. The dissolution rate of Specimen 1 A is almost same as that of Specimen 1, while Specimen 2 and 3 showed 2.15 times and 4.31 times larger dissolution rate than Specimen 1. EIS test showed that the larger the sintering vacuum degree was applied, the more anodic reaction was accelerated and the less corrosion resistance was observed. Alternate wetting and drying test clarified that Specimen 1 A had the best corrosion resistance, while Specimen 3 had the worst, which agrees well with the results of polarization curve measurement and EIS test.

• 社団法人粉体粉末冶金協会の論文
• 2007-07-15

著者

• Majima Kazuhiko

  Graduate School Of Science And Engineering For Research University Of Toyama

• Sunada Satoshi

  Graduate School Of Science And Engineering For Research University Of Toyama

• Tanaka Shigeo

  Taisei Kogyo Co. Ltd.

• YAMAMOTO Takahisa

  Graduate School, University of Toyama

• KADA Norio

  Taisei Kogyo Co., Ltd.

• Kada Norio

  Taisei Kogyo Co. Ltd.

• Yamamoto Takahisa

  Graduate School University Of Toyama

• TANAKA Shigeo

  Taisei Kogyo Co., Ltd.

関連論文

• Processing of polymer-derived porous SiC body using allylhydridopolycarbosilane (AHPCS) and PMMA microbeads
• Corrosion Behavior of Pure Titanium by MIM Process under SSRT Condition
• Influence of sintering atmosphere on the corrosion behavior of the type 410 stainless steel prepared by MIM process (特集 自動車用焼結部品の更なる拡大)
• Micro Metal Injection Molding Process and It's Application(Synergy by Microparticulation)

スポンサーリンク