Nd-Fe-B磁石特性に及ぼす結晶配向の影響
スポンサーリンク
概要
- 論文の詳細を見る
Grain alignment is one of a factor affecting coercive force in Nd-Fe-B sintered magnets. Relation between degree of alignment and coercive force was evaluated using Br/Js as the degree of grain alignment. It was found that the coercive force decreases with alignment increase in highly aligned region. The decrease ratios of coercive force with various alignments to the isotropic magnets coercive forces are on the same line even though they have different coercive force due to different composition in isotropic aligned state. Extrapolating this line to perfectly aligned magnet, coercive force of perfectly aligned magnet reaches to −30% of coercive force of the isotropic oriented magnets.It is found that this coercive decrease ratio behavior is similar even in ferrite magnets. We estimate coercive force of perfectly aligned magnets from isotropic magnet and obtained 1/√2 (0.70) of isotropic magnets coercive force which is agrees well to our experimental result.
- 2006-03-15
著者
-
細川 誠一
日立金属(株)磁性材料研究所
-
播本 大祐
(株)NEOMAX開発本部 研究開発センタ
-
松浦 裕
(株)NEOMAX開発本部 研究開発センタ
-
細川 誠一
(株)NEOMAX開発本部 研究開発センタ
関連論文
- SUS316Lステンレス鋼とFe-47Niパーマロイの圧紛体の組み合わせ焼結接合
- Nd-Fe-B磁石特性に及ぼす結晶配向の影響
- MIMバインダを用いた磁性粉の新しい配向成形の試み
- Srフェライトの配向度に及ぼす粉砕粒度と成形磁界の影響
- Ca-La-Co系M型フェライトの組成と磁気特性
- ハードフェライト粉の圧縮成形過程における保磁力の低下に及ぼす圧力の作用状態の影響
- Srフェライト粉とその成形体の磁気特性に及ぼすメカノフュージョン処理の影響
- 926 ハードフェライト粉の圧縮成形過程における保磁力の低下に及ぼす圧力の作用状態の影響
- 磁界配向したSr-フェライト圧粉体の組み合わせ焼結接合
- 紫外線硬化樹脂を用いた磁性粉末の配向成形
- Srフエライト粉末を用いたボンド磁石の磁気特性に及ぼす成形条件の影響
- Sr-フエライトの収縮異方性と組み合わせ焼結結合への応用
- 焼結接合法によるフェライト部品の作製