PET繊維・鋼繊維補強モルタルの一軸引張特性
スポンサーリンク
概要
- 論文の詳細を見る
Concrete or mortar is one of the fragile materials that possess low tensile strength and relatively high compressive strength. The addition of fibers randomly distributed in the matrix, substantially improves their mechanical performance such as post-cracking strength in compression, strength/toughness (energy required up to failure) in bending, impact strength, fatigue strength and also wear resistance. Fiber reinforced concrete/mortar (FRC/FRM) had been gaining various application fields; tunnel support, dam site, river facilities, road pavement and floor in building.In this study, uniaxial tension tests of steel/PET fiber reinforced mortar (SFRM/PET-FRM) were conducted by servo-controlled testing machine to obtain stress-displacement curves. The experimental results can be summarized;1) After mortar was cracked, stress induced by pullout resistance of fibers was observed.2) The displacement of PET-FRM at which stress took the post-cracking peak value (post-cracking strength) was considerably larger than that of SFRM.3) The stress/force-displacement curves of SFRM/PET-FRM can be estimated by the results of a single steel/PET fiber pullout tests.4) As far as SFRM is concerned, the number of fibers observed on the fractured surface is smaller than that on mechanically sectioned surface. In case of PET-FRM, no difference is found in the number of fibers between the fractured and the sectioned surface.
- 2006-03-25
著者
-
福井 勝則
東京大学 工学系研究科 システム創成学専攻
-
大久保 誠介
東京大学 工学系研究科 システム創成学専攻
-
大久保 誠介
東京大学工学部
-
大久保 誠介
東大・工
-
大久保 誠介
東京大学 大学院工学系研究科
-
宮崎 晋行
東京大学大学院工学系研究科 地球システム工学専攻
-
宮崎 晋行
(独)産業技術総合研究所 メタンハイドレート研究ラボ
-
大久保 誠介
東京大学大学院工学系研究科地球システム工学
-
宮崎 晋行
東京大学大学院 工学系研究科
関連論文
- 飛騨トンネル本坑におけるTBMのディスクカッタの摩耗
- 衝撃貫入試験におけるボタンビットの貫入特性
- 西松の切削抵抗の式にもとづいたトンネル掘進機のずりの形状・寸法の推定
- 鋼繊維とPET繊維補強モルタルの4点曲げ特性
- PET繊維・鋼繊維補強モルタルの一軸引張特性
- 鋼繊維補強モルタルの耐久性に関する研究
- 衝撃貫入試験におけるボタンビットの貫入特性
- ポリオレフィン繊維のコンクリートとの付着特性と埋込角度・長さの影響
- 岩石の強度とクリープ寿命の分布特性に関する一考察
- 岩盤の破壊基準と長期強度に関する一考察