Phase Equilibria in High MgO Ferro-manganese and Silico-manganese Smelting Slags

スポンサーリンク

概要

• 論文の詳細を見る

• Liquidus isotherms and phase equilibria have been determined experimentally for a pseudo-ternary section of the form “MnO”-(CaO+MgO)-(SiO2+Al2O3) with a fixed Al2O3/SiO2 weight ratio of 0.17 and MgO/CaO weight ratio of 0.17 for temperatures in the range 1473-1673 K.The primary phase fields present for the section investigated include manganosite (Mn,Mg,Ca)O; dicalcium silicate α-2(Ca,Mg,Mn)O · SiO2; merwinite 3CaO · ((Mg,Mn)O · 2SiO2; wollastonite [(Ca,Mg,Mn)O · SiO2]; diopside [(CaO,MgO,MnO,Al2O3) · SiO2]; tridymite (SiO2); tephroite [2(Mn,Mg)O · SiO2]; rhodonite [(Mn,Mg)O · SiO2] and melilite [2CaO · (MgO,MnO,Al2O3) · 2(SiO2,Al2O3)].The liquidus temperatures relevant to ferro-manganese and silico-manganese smelting slags have been determined. The liquidus temperature is shown to be principally dependent on the modified basicity weight ratio (CaO+MgO)/(SiO2+Al2O3) at low MnO concentrations, and dependent on the mole ratio (CaO+MgO+MnO)/(SiO2+Al2O3) at higher MnO concentrations.

• 2005-07-15

著者

• Hayes P.

  Pyrosearch Pyrometallurgy Research Centre School Of Engineering The University Of Queensland

• ZHAO B.

  PYROSEARCH, Pyrometallurgy Research Centre, School of Engineering, The University of Queensland

• JAK E.

  PYROSEARCH, Pyrometallurgy Research Centre, School of Engineering, The University of Queensland

関連論文

• Phase Equilibria in High MgO Ferro-manganese and Silico-manganese Smelting Slags

スポンサーリンク