Corrosion Resistance of a Stabilized ZrO_2 Tundish Nozzle Densified with Monoclinic ZrO_2 Particles
スポンサーリンク
概要
- 論文の詳細を見る
- 1997-12-01
著者
-
SASAKI KIMIAKI
Kawasaki Refractories Co., Ltd.
-
TANAKA SEIJIRO
Kawasaki Refractories Co., Ltd.
-
Sasaki Kimiaki
Dept. Of Product Development
-
Tanaka Seijiro
Research Laboratories Kawasaki Refractories Co. Ltd
-
Sasaki Kimiaki
Kawasaki Refractories Co. Ltd.
-
Maeda Eizo
Research Laboratories Kawasaki Refractories Co. Ltd
-
Saito Masanobu
Research Laboratories Kawasaki Refractories Co. Ltd
-
SAITO MASANOBU
Kawasaki Refractories Co., Ltd.
-
Tanaka Seijiro
Kawasaki Refractories Co.
-
MAEDA EIZO
Kawasaki Refractories Co., Ltd.
-
Maeda Eizo
Kawasaki Refractories Co. Ltd.
-
Saito Masanobu
Kawasaki Refractories Co. Ltd.
関連論文
- High Performance Magnesia-Carbon Ladle Brick for VOD Process
- Wear Mechanisms for Tundish Castables
- The Effect of Cement Composition on the Explosive Spalling of Castables
- Effect of Slag Compositions on the Wear of Castables
- Evaluation of the Lining Life of an Alumina-Magnesia Castable
- Influence of SiO_2 Content on Bonding Characteristics of Mud for Blast Furnace Tap Hole
- Development of a High Density Taphole Mud
- Development of a Stabilized ZrO_2 Tundish Nozzle Impregnated with Monoclinic ZrO_2
- Influence of Microstructure of Alumina-Zirconia Grain on Thermal Shock Resistance of Refractories
- Corrosion Mechanism of Slag-Line Materials in Blast Furnace Main Trough
- An Evaluation Method for Tundish Castable
- Effect of CaO Distribution and Grain Boundary Phases on the Properties of CaO-rich Fused MgO
- Relationship between Grain Size Distribution and Fluidity in Castable Refractories
- Improving the Life of Alumina-Silica Castable for Tundish
- Optimizing the Wear Rate of Metal Line Castables for Blast Furnace Main Troughs
- Improvement of the Slaking Resistance of Basic Refractories
- Improvement of Castables for Hot Metal Pre-Treatment Lances
- Relationships between Setting Time and Additives in Castables
- Structure Change of Alumina Castable by Addition of Magnesia or Spinel
- Improvement of Alumina-Spinel Castables for Steel Ladles
- Improvement of the Service Life of an Alumina-Silica Castable for Tundishes (Part 2)
- Corrosion Resistance of Densified Zirconia Tundish Nozzle
- Corrosion Resistance of a Stabilized ZrO_2 Tundish Nozzle Densified with Monoclinic ZrO_2 Particles
- Desire for More Scientific Research in Refractories
- Damage of Tundish Linings
- Adsorption of Silica onto the Surface of Cement Particles in Castable
- Mechanism of Crack Formation in Alumina-Based Castable Refractories
- Influence of Raw Particle Characteristics on Slip Casting
- Reaction between Alumina Cement and Phosphate
- Effect of Particle Size Distribution of Binary Powder Mixtures on Slurry Viscosity