Liquidus Relationships in the CaO-corner of the Ternary System CaO-Al_2O_3-SiO_2
スポンサーリンク
概要
- 論文の詳細を見る
Saturation lines of CaO, 2CaO·SiO<SUB>2</SUB> and 3CaO·SiO<SUB>2</SUB> in the system CaO-Al<SUB>2</SUB>O<SUB>3</SUB>-SiO<SUB>2</SUB> were determined at 1600 and 1700°C using a technique of solid phase dissolution in a liquid slag phase. The liquidus surface of 3CaO·SiO<SUB>2</SUB> phase was found to be larger than expected. The solubility of 2CaO·SiO<SUB>2</SUB> was found to be higher, especially at 1700°C, and the CaO solubility was found to be lower then previously known. Finally, the solubility of 2CaO·SiO<SUB>2</SUB> in the binary system CaO-SiO<SUB>2</SUB> was determined to be 2.5-3 wt% higher than in the currently accepted system.
- The Iron and Steel Institute of Japanの論文
- 1996-12-15