Electrochemical Evaluation for Defects in TiN Films Coated on SUS 304 Stainless Steel

スポンサーリンク

概要

• 論文の詳細を見る

• The amount of defects in TiN films coated on SUS304 stainless steel has been evaluated by three electrochemical measuring techniques in a sulfuric acid solution containing potassium thiocyanate. Three different TiN films were prepared by a hollow cathode ion plating technique. A critical passivation current density (<I>i</I><SUB>crit</SUB>) can readily provide the apparent amount of the defects. However, this method was found to overestimate the amount of the defects because active dissolution of the substrate at the measurement caused enlargement of the defects. An activation time, which is a period until free corrosion potential (<I>E</I><SUB>corr</SUB>) descends to that of the bare substrate steel, was not useful to evaluate the amount of defects rapidly because about a half the specimens did not activate within a test time of 90 ks. More precise and less destructive evaluation could be achieved by using a reciprocal of polarization resistance (<I>R</I><SUB><I>P</I></SUB><SUP>-1</SUP>) which was obtained by an electrochemical impedance spectroscopy immediately after activation. It is concluded that <I>i</I><SUB>crit</SUB> is a suitable parameter for an approximate estimation of the defect area, and <I>R</I><SUB><I>P</I></SUB><SUP>-1</SUP> amount of the original defects.

• 社団法人 日本鉄鋼協会の論文
• 1995-05-15

著者

• Shibata Toshio

  Department Of Materials Science And Processing Faculty Of Engineering Osaka University

• HARUNA Takumi

  Department of Materials Science and Processing, Faculty of Engineering, Osaka University

• Haruna Takumi

  Department Of Materials Science And Processing Faculty Of Engineering Osaka University

• SHIBATA TOSHIO

  Department of Chemical Engineering, Osaka University

関連論文

• Failure of Scales Formed on Cu-containing Low Carbon Steels during Cooling
• Effect of Nb-Ion Implantation on the Oxidation Resistance of TiAl
• Improvement in High-Temperature Oxidation Resistance of TiAl by Addition of 0.2 mass% Zr
• Electrochemical Evaluation for Defects in TiN Films Coated on SUS 304 Stainless Steel
• 方形波電位パルス法によるFe-Ti合金上へのTiリッチ酸化物層の生成とその特性
• Development of Scanning Laser-Enhanced Electrochemical Microscopy for Visualizing Hydrogen Distribution on a Steel
• Influences of Potential and pH on Initiation of Environment-Assisted Cracking of Ti-6Al-4V
• BEHAVIOR OF RISING BUBBLES IN A GAS-FLUIDIZED BED AT ELEVATED TEMPERATURE
• Corrosion Resistance of Titanium-Magnesium Alloy in Weak Acid Solution Containing Fluoride Ions

スポンサーリンク