Density of Liquid IF Steel Containing Ti
スポンサーリンク
概要
- 論文の詳細を見る
Density of liquid IF Steel containing Ti was measured with the modified sessile drop method at a temperature range from 1530 to 1610°C. Densities of pure molten Fe measured at a temperature range between 1550°C and 1600°C were quite close to those obtained by Saito et al., but a little lower than their results at temperature higher than 1600°C. Thermal expansion coefficient of molten IF steel containing Ti increased linearly with an increase in titanium content. The density of the liquid IF steel was described as a function of the temperature and Ti content as follows:ρ=7.05-4.73×10-2[%Ti]-(1.05+0.66[%Ti])×10-3(T-1530)
- 社団法人 日本鉄鋼協会の論文
- 2005-03-15
著者
-
MUKAI Kusuhiro
Department of Materials Science and Engineering, Faculty of Engineering, Kyushu Institute of Technol
-
Mukai Kusuhiro
Department Of Materials Science And Engineering Faculty Of Engineering Kyushu Institute Of Technolog
-
Mukai K
Department Of Materials Science And Engineering Kyushu Institute Of Technology
-
ZEZE Masafumi
Yawata R&D Laboratory, Nippon Steel Corporation
-
ZHONG Liangcai
Institute of Ferrous Metallurgy, Northeastern University
-
Zeze M
Yawata R&d Laboratory Nippon Steel Corporation
-
Zeze Masafumi
Yawata R&d Lab Nippon Steel Corp.
-
ZHONG L.
Kyushu Institute of Technology
-
Mukai Kusuhiro
Department Of Materials Sciece And Engineering Faculty Of Engineering Kyushu Institute Of Technology
-
Zeze Masafumi
Yawata R & D Laboratories, Nippon Steel Corporation
関連論文
- Influence of Injected Ar Gas on the Involvement of the Mold Powder under Different Wettabilities between Porous Refractory and Molten Steel
- Measurement of the Density of Ni-Cr Alloy by a Modified Pycnometric Method
- Numerical Analysis of Nitrogen Absorption Rate Accompanied with Marangoni Convection in the Molten Iron under Non-inductive Stirring Condition
- Influence of Wettability on the Behavior of Argon Bubbles and Fluid Flow inside the Nozzle and Mold
- Loacl Corrosion of Solid Silica at the Surface of Molten Silicon
- Determination of Aluminum and Oxygen Contents in Liquid Iron in Equilibrium with α-Alumina and Hercynite
- Interfacial Properties of Molten Low Carbon Steel Containing Ti, Nb or B in Relation to the Behavior of Fine Particles in Continuous Casting Process
- Density of Liquid IF Steel Containing Ti
- Measurement of the Densities of Nickel-Based Ternary, Quaternary and Commercial Alloys
- Measurement of the Density of Binary Ni-X (X=Co, W, Ta, Al) Alloys
- Observation of Inclusion in Aluminum Deoxidized Iron
- Reply to the Paper Named "The Force Acting on a Sphere Moving towards a Solidification Front due to an Interfacial Energy Gradient at the Sphere/Liquid Interface"
- Surface Tension and Wettability of Liquid Fe-16mass%Cr-S Alloy with Alumina
- Effects of S and N on Surface Tension of Liquid Fe-16mass%Cr Alloy and its Wettability with Alumina
- Surface Tension and Wettability of Liquid Fe-16 mass%Cr-O Alloy with Alumina
- Surface Tension and Wettability of Liquid Fe-l6mass%Cr-O Alloys with Alumina
- The Influence of Oxygen on the Rate of Nitrogen Absorption into Molten Iron and Marangoni Convection
- Measurement of Temperature Fluctuations in Marangoni Convection in a Half-zone Silicon Melt on Board the TR-IA-4 Rocket (特集 TR-IA4号機)
- Density of Ni-Cr Alloy in Liquid and Solid-Liquid Coexistence States
- Thermodynamic Analysis on Metastable Alumina Formation in Aluminum Deoxidized Iron Based on Ostwald's Step Rule and Classical Homogeneous Nucleation Theories
- Spout Eye Area in Ladle Refining Process
- Model Experiments on the Mixing Time in a Bottom Blown Bath Covered with Top Slag
- Behavior of Fine Bubbles in Front of the Solidifying Interface
- Behavior of Penetration and Dissolution between Solid CaO and Molten Slag
- Rayleigh-Taylor Instability in the Process of Clad Steel Slab Casting with Level DC Magnetic Field
- The Rate of Nitrogen Desorption from Liquid Iron by Blowing Argon Gas under the Condition of Non-inductive Stirring
- Wettability of Zirconia and Alumina Ceramics by Molten Zinc
- Application of Barium-bearing Alloys in Steelmaking
- Measurement of the Density of Molten Silicon by a Modified Sessile Drop Method
- Wettability of Ceramics with Molten Silicon at Temperatures Ranging form 1693 to 1773K
- Effects of Boron and Carbon on the Surface Tension of Molten Silicon under Precisely Controlled Oxygen Partial Pressure
- The Surface Tension of Liquid Iron Containing Nitrogen and Oxygen
- Correspondence between Surface Tension Estimated by a Surface Thermodynamic Model and Number of Bubbles in the Vicinity of the Surface of Steel Products in Continuous Casting Process
- Stability of Two Stratified Liquid-metal Layers in an Uniform DC Magnetic Field.