Thermal Characteristics of Silica-free Porous Material for Submerged Entry Nozzles
スポンサーリンク
概要
- 論文の詳細を見る
- 2004-09-01
著者
-
Ogata Koji
Krosaki Harima Corp.
-
ASANO KEISUKE
Krosaki Harima Corp.
-
Ogata Koji
Krosaki Corp.
-
Amano Jiro
Technical Research Center Krosaki Harima Corporation
-
Asano Keisuke
Technical Research Center Krosaki Harima Corporation
-
MORIKAWA KATSUMI
Technical Research Center, Krosaki Harima Corporation
-
AMANO JIRO
Krosaki Harima Corp.
-
FUKAI KEIKI
Krosaki Harima Corp.
-
MORIKAWA KATSUMI
Krosaki Harima Corp.
-
Morikawa Katsumi
Technical Research Center Krosaki Harima Corporation
-
Asano Keisuke
Krosaki Corporation
関連論文
- Effect of ZrO_2 Material Properties on the Durability of ZrO_2-C Material
- Discussion of a Method for Evaluation of Refractory Creep
- Nonlinear Finite Element Analysis of Nozzles for Continuous Casting
- Evaluation of Corrosion Resistance by Molten Iron Oxide of Refractories for Continuous Casting
- Effect of ZrO_2 Content on Properties of Al_2O_3-ZrO_2-C Materials for Slide Gate Plate
- Effect of Metallic Silicon on Properties of Burnt Sliding Nozzle Plate (Part 2)
- Corrosion Resistance of Alumina-Graphite, Alumina-Zirconia-Graphite, and Zirconia-Graphite Refractories to Molten Steel
- Inhibition of the Expansion of Magnesia-Added Alumina-Graphite Material Used for Ladle Shroud
- Development of Porous Material for Gas Purging Plugs
- Quantitative Analysis of the Penetration of Molten Silver into Porous Refractories
- Direct Observation of the Penetration of Molten Silver into Porous Refractory
- Analysis of the Penetration Behavior of Molten Silver into Porous Refractory
- Direct Observation on the Penetration of Molten Silver into Porous Refractory
- Physical Properties and Microstructure of Silica Raw Materials and Their Effects on Phase Transformation
- Evaluation of Slaking Resistance of MgO-C Bricks used for RH Degasser
- Auger (AES) Analysis of Carbon in Carbon-Silicon Composite Materials
- Crystallizing Behavior of Amorphous Silica Material Caused by Annealing
- Effects of Surface Properties of Alumina Raw Materials on Properties of SN Plate Bricks
- Expansion Behavior of Alumina-Magnesia Castables
- Effect of Carbon Raw Materials on the Properties of Alumina Carbon Brick
- Thermal Shock Resistance of Al_2O_3-ZrO_2-Carbon Sliding Gate Plate
- Effect of Carbon Content on the Thermal Characteristics of MgO-C Bricks for BOF
- Effect of Total Iron (T. Fe) Content of Slag on Corrosion of MgO-C Bricks
- Spalling Resistance and Physical Behavior of MgO-C Refractories at High Temperature
- Effect of Metallic Powder Combinations on the Corrosion of MgO-C Bricks
- Effect of Magnesium Powder Addition on Corrosion Resistance of MgO-C Bricks
- Comparison of Spalling Resistances of Unburned and Burned Magnesia-Carbon Bricks
- Effect of MgO Aggregate on the Thermal Characteristics of Magnesia-Spinel Bricks
- Drying Characteristics of Castables
- Fatigue Fracture of Magnesia-spinel Bricks by Cyclic Loading
- Evaluation of Slaking Resistance of MgO-C Bricks Used for RH Degasser
- Relationship between MgO Aggregate Purity and Properties of MgO-C Brick after Firing in a Reducing Atmosphere
- The Effect of the Refractory Composition on Erosion Resistance
- Thermal Characteristics of Silica-free Porous Material for Submerged Entry Nozzles
- Improving the Corrosion Resistance of Silica-Free Alumina Graphite for the Slagline of Ladle Shrouds by the Addition of Magnesia
- Development of Chrome-Free Porous Refractories
- Use of Metal Powder in Wet Spray Materials
- Thermal Shock Testing of Continuous Casting Nozzles with Molten Iron, by a New Test Method
- Thermal Stress Analysis of Nozzles for Continuous Casting
- Effect of Low Thermal Expansion Raw Material on Microstructure and Spalling Resistance of Sliding Nozzle Plates
- MgO-Cr_2O_3 Insert Ring for SN Upper Nozzles
- Effect of Binder on the Sealing Property of Refractory Joint Seal Material
- Iron Oxide Resistance of Alumina-Spinel Castable
- Effect of Fused Silica on the Permeability of Slit-Type Submerged Entry Nozzles
- Effect of MgO Purity on the Corrosion Resistance of MgO-C Bricks against High Temperature Iron Oxide Slag
- Application of Nano Technology to MgO-C Bricks
- Effect of Alumina Grain Size and Fused Silica Contents on Refractory Properties
- Properties of High Zirconia-Graphite Material for Submerged Entry Nozzles
- Effect of Apparent Porosity on the Corrosion Index of Zirconia-Graphite, with Higher ZrO_2 Content
- Influence of Apparent Porosity on Corrosion Resistance of ZG Materials
- Influence of the Quantity of Carbon Originating in a Resin on the Gas Permeation Character of Submerged Entry Nozzle (SEN) Materials
- Taphole Clay Containing Shungite Raw Material
- Examination of Tap-Hole Clay Plasticity
- Hole-Filling Characteristics to Evaluate Taphole Clay
- Development of Taphole Clay with Excellent Expandability Inside the Blast Furnace
- Effect of Extrusion Pressure on Blast Furnace Tap Hole Mixes
- Influence of Spinel Clinker on Corrosion Resistance of BF Trough Castable
- Provide No. 1 Value to Customers Worldwide
- Effect of Dense Low Expansion ZrO_2 System Raw Material Addition on Properties of SN plates
- Improvement in Surface Damage of SN Plate Material by Modification in Bonding Form