Fatigue Crack Initiation in an Interstitial Free Steel
スポンサーリンク
概要
- 論文の詳細を見る
The initiation of small cracks has been studied on dumble-shaped plate type specimens of an interstitial free (IF) steel at the load ratio of R=0 under varied cyclic stress amplitudes between 0.6 and 1.0 of yield stress. Nucleation of cracks were observed at ferrite-ferrite grain boundary (FFGB) as well as inside ferrite grain body (FGB), but the former location was found to be the preferred one. The average length of FFGB cracks is found larger than that of the FGB cracks for identical cyclic loading conditions. The formation of slip bands inside the grain body, slip band impingement at grain boundary and elastic-plastic incompatibility synergistically influence the event of crack initiation in the investigated steel. In addition, nucleation of voids inside slip bands was found to be a new phenomenon associated with the above possibilities to affect the nucleation of cracks in the investigated steel.
- 社団法人 日本鉄鋼協会の論文
- 2005-01-15
著者
-
Chakraborti P.
Department Of Metallurgical Engineering Jadavpur University
-
Maiti R.
Department Of Metallurgical And Materials Engineering Indian Institute Of Technology
-
NARASAIAH N.
Department of Metallurgical and Materials Engineering, Indian Institute of Technology
-
RAY K.
Department of Metallurgical and Materials Engineering, Indian Institute of Technology
-
Narasaiah N.
Department Of Metallurgical And Materials Engineering Indian Institute Of Technology
-
Ray K.
Department Of Metallurgical And Materials Engineering Indian Institute Of Technology