Decarbonization Behavior of Graphite-Containing Refractories by Molten Steel
スポンサーリンク
概要
- 論文の詳細を見る
- 1999-12-01
著者
-
Uchida Shigeki
Research Center Shinagawa Refractories Co. Ltd.
-
Uchida Shigeki
Shinagawa Refractories Co. Ltd.
-
Nakamura Ryosuke
Shinagawa Refractories Co. Ltd.
-
Nomura Osamu
Shinagawa Refractories Co. Ltd.
-
LIN WEI
Shinagawa Refractories Co., Ltd.
-
MORI EIICHIROU
Shinagawa Refractories Co., Ltd.
-
Mori Eiichirou
Shinagawa Refractories Co. Ltd.
-
Lin Wei
Research Center Shinagawa Refractories Co. Ltd.
-
Lin Wei
Shinagawa Refractories Co. Ltd.
関連論文
- Structural Analysis of the Tap Hole in Converters
- Synthesis of Al_4O_4C from Starting Raw Materials of Alumina and Graphite
- Formation of ZrC and Its Effect on the Penetration of Molten Steel into ZrO_2-C Refractory
- Improvement in Thermal Spalling Resistance of Burner Tile Refractory
- Formation of ZrC in ZrO_2-C Materials and Its Effect on Molten Steel Penetration
- Reactivity of Submerged Entry Nozzle to Molten Steel
- Behavior of Metal Additives on Low-Carbon MgO-C Bricks
- Suppression Effects of Aluminum on Oxidation of MgO-C Bricks
- Evaluation of Layer Thickness to Reduce the Thermal Stress in Multilayer Submerged Entry Nozzles
- Effect of Layer Thickness in Reducing Thermal Stress in Multilayer Submerged Entry Nozzles
- Environmently Friendly MgO-C Products with Non-Phenol Resin
- Magnesia-Spinel Bricks for Refining Furnaces
- Low-Flux Magnesia-Chrome Bricks for Tuyeres in AOD Vessels
- Water Model Simulation of Annular-Stepped Submerged Entry Nozzle (III)
- Water Model Simulation of an Annular Step Submerged Entry Nozzle
- Development of an Al-Fe-O Composition That Prevents Alumina Clogging in SEN's
- Slag-coating Behavior of Al_2O_3-SiO_2-C Materials
- Heat-Transfer Analysis of Various Ladle Lining Refractories
- Low Permeability Magnesia-Chrome Bricks for AOD and VOD Vessels
- Iron-Oxide Corrosion of Magnesia-Chrome Bricks in the RH-OTB Degasser
- Development of a Submerged Entry Nozzle for Casting High Oxygen Steel
- Decarbonization Behavior of Graphite-Containing Refractories by Molten Steel
- Quantitative Simulation of Cracks Generated in Slide Gate Valve Plates
- Quantitative Simulation of Cracks Generated in SV Plate
- Rotary Slag Test of Magnesia-Chrome Brick Using Step Specimen
- Development of Low Thermal Expansion MgO-C Bricks
- Application of Low Thermal Conductivity MgO-C Brick for Steel Ladle
- Development of a High Strength Slide Gate Plate
- Evaluation Method for Drilled-Ability of Tap-Hole Clay
- Damage in Taphole Clay and Required Properties
- Effect of Si Addition on the Strength of Taphole Mix
- Development of Castables for Roof of Ash Melting Furnaces
- Thermal Properties of Shotcreting Material for Steel Ladles
- Insulating Material for Shotcreting System
- Development of Basic Castables for Shotcreting
- Remain Steadfast During Turbulent Days
- Shotcrete Material for Repairing Hot Metal Pretreatment Vessels
- Reaction between SiC and Binders in Monolithic Refractories
- Simplified Wet Gunning Method for Small Scale Repairs
- The Effect of Added Spinel on Castables for Blast Furnace Troughs(2)
- Use of Low Thermal Conductivity MgO-C Bricks in Steel Ladles
- Application of Low Thermal Conductivity MgO-C Bricks in Steel Ladles
- Improved Design of a Ladle Bottom Lining
- Blast Furnace Trough Materials : Performance and Environmental Considerations
- Installation Method of New Wet Type High Density Gunning Castable
- Development and Application of a Hot Abrasion Test Apparatus
- Numerical Analysis of Stress and Displacement of Rotary Kiln Bricks under Thermal and Mechanical Loads
- Development of an Automatically Operated Thermal Expansion Apparatus
- Structural Analysis of the Cone Lining in BOF Converters
- FEM Analysis of Load Applied to Wedge Anchor Carrying BOF Brick