The Effects of Solute and Vacancy Depletion on the Formation of Precipitation-Free Zone in a Model Binary Alloy Examined by a Monte Carlo Simulation

スポンサーリンク

概要

• 論文の詳細を見る
• Japan Institute of Metalsの論文
• 2004-05-20

著者

• OCHIAI Shojiro

  International Innovation Center, Kyoto University

• OKUDA Hiroshi

  International Innovation Center, Kyoto University

• Ochiai Shojiro

  International Innovation Center Kyoto University

• Okuda H

  International Innovation Center Kyoto University

関連論文

• Degradation Mechanism of Amorphous Silicon Carbide Fiber due to Air-Exposure at High Temperatures
• Thermomechanical Analysis of Micromechanical Formation of Residual Stresses and Initial Matrix Failure in CFRP(Advanced Technology of Experimental Mechanics)
• OS9(3)-10(OS09W0090) Monte Carlo Simulation on Fracture Behavior of Unidirectional Fiber Reinforced Ceramics Based on Mesomechanics
• OS9(2)-8(OS09W0185) Micromechanical Stress Formation and Initial Matrix Failure in Fiber Model Composites under Consideration of Plastic Deformation during Cooling Down
• Nonlinear Micromechanical Analysis of the Formation of Residual Stresses and Initial Matrix Failure in CF/Epoxy
• Parallel Performance of GeoFEM and Its Applications to Solid Earth Problems
• GeoFEM : Multi-Purpose Parallel FEM for Solid Earth : (1) Project Overview
• Analysis of Buckling and Interfacial Debonding of Galvannealed Coating Layer on Steel Substrates under Applied Tensile Strain
• The Effects of Solute and Vacancy Depletion on the Formation of Precipitation-Free Zone in a Model Binary Alloy Examined by a Monte Carlo Simulation
• Crack Spacing Distribution in Coating Layer of Galvannealed Steel under Applied Tensile Strain

スポンサーリンク