Thermoelectric Properties of FeSi Thermoelectric Element Produced by Utilizing the MA/SPS Process

概要

論文の詳細を見る
P-type and n-type β-FeSi2 was produced by utilizing the process of mechanical alloying(MA)and spark plasma sintering(SPS)technique. Raw powders of pure iron, silicon, manganese and cobalt were mixed and mechanically alloyed for 72ks using planetary ball mill. The mixing fractions of the powders were in accordance with the mole fractions of the Fe0.92Mn0.08Si2 (p-type) and Fe0.98Co0.02Si2 (n-type), respectively. The SPS temperature for producing p-type β-FeSi2 was 1073-1153 K and n-type β-FeSi2 was 1073-1173 K, and the holding time was 0.3ks. When the sintering temperature was over these temperatures, α-FeSi2 was produced and thermoelectric properties were reduced. The density of p-type β-FeSi2 sintered at 1153 K was 4.64g/cm3(the relative density was 94.1%), and the maximum power factor was 0.30mW/mK2 at 850 K. The density of n-type β-FeSi2 sintered at 1173K was 4.71 g/cm3(the relative density was 95.5%), and the maximum power factor was 0.058 mW/mK2 at 650K.
社団法人粉体粉末冶金協会の論文
2003-11-15