Effect of Morphology of Copper Precipitation Particles on Hydrogen Embrittlement Behavior in Cu-Added Ultra Low Carbon Steel
スポンサーリンク
概要
- 論文の詳細を見る
- Japan Institute of Metalsの論文
- 2002-09-01
著者
-
Misawa Toshihei
Department Of Materials Science And Engineering Faculty Of Engineering Muroran Institute Of Technolo
-
Komazaki Shin-ichi
Department Of Materials Science And Engineering Muroran Institute Of Technology
-
Komazaki Shin-ichi
Department Of Machine Intelligence And Systems Engineering Akita Prefectural University
-
KOYAMA Akinobu
Department of Materials Science and Engineering, Muroran Institute of Technology
-
Koyama Akinobu
Department Of Materials Science And Engineering Muroran Institute Of Technology
関連論文
- Effect of Laves Phase on Hydrogen Behavior in V-Zr-Ti-Ni Hydrogen Absorption Alloys
- Observation of Tritium Distribution in V-4Cr-4Ti alloy by Tritium Radioluminography
- Observation of Hydrogen Distribution in V_Cr_Ti_ Alloy by Tritium Radioluminography
- In-Situ Micro-Raman Scattering Investigation of LaNi_Co_Mn_Al_ Metal Hydride under Hydrogen Atmosphere
- Visualization of Hydrogen Location in Pure Vanadium using an Imaging Plate Detector
- Evaluation of Susceptibility to Hydrogen Embrittlement of 7075 Aluminum Alloy by Hydrogen Addition Using Flax-Treatment Method
- Damage Evaluation of a Welded Joint in a Long-term Service-exposed Boiler by Using a Small Punch Creep Test
- Creep Life Prediction of Ni-Base Superalloy Used in Advanced Gas Turbine Blades by Electrochemical Method
- Observation of Hydrogen Distribution on Pt, Pd and Type 304 Austenitic Stainless Steel by Silver Decoration Method
- Small Punch Creep Behavior of Service-Exposed SUS 316 HTB Superheater Boiler Tube(High Temperature Materials)
- Size Effect of Copper Precipitation Particles on Electrochemical Nanoscopic Galvanic Behavior in Cu-Added Ultra Low Carbon Steel
- In-situ Observation of Dynamic Reacting Species at Pit Precursors of Nitrogen-bearing Austenitic Stainless Steels
- In Situ Observation of Preferential Anodic Dissolution of Phosphorus Compound in Fe-P Alloys Using Raman Spectroscopy
- Structure of Protective Rust Layers Formed on Weathering Steels by Long-term Exposure in the Industrial Atmospheres of Japan and North America
- APPLICATION OF SMALL PUNCH TEST TO EVALUATE DBTT, FRACTURE TOUGHNESS, CORROSION RESISTANCE AND SCC SUSCEPTIBILITY OF STRUCTURAL STEELS USING MINIATURIZED SPECIMENS : MATERIAL DEGRADATION EVALUATION
- Effect of Applied Cathodic Potential on Susceptibility to Hydrogen Embrittlement in High Strength Low Alloy Steel
- Effect of Morphology of Copper Precipitation Particles on Hydrogen Embrittlement Behavior in Cu-Added Ultra Low Carbon Steel
- Preface to the Special Issue on "Hydrogen Behavior in Environmental Degradation"