Deformation Behavior of Low Carbon TRIP Sheet Steels at High Strain Rates
スポンサーリンク
概要
- 論文の詳細を見る
Two high strength transformation-induced plasticity (TRIP) sheet steels with 0.10 wt% and 0.14 wt% carbon were produced with retained austenite volume fractions varying from less than 3% up to 16%. These TRIP steels were tensile tested at strain rates ranging from 10−3 to 2.5×102 s−1 to determine the effects of strain rate and retained austenite volume fraction on tensile properties. Increasing the retained austenite volume fraction increases UTS, total elongation, uniform strain and total absorbed energy, but decreases yield strength and absorbed energy below 10% engineering strain. Increasing strain rate increases yield strength and UTS, and creates a better-defined yield point, but has little effect on strain hardening behavior for TRIP steels with 11% or less retained austenite. The TRIP steel with 16% retained austenite shows increasing strain hardening rate with strain rate at low strains.
- 社団法人 日本鉄鋼協会の論文
- 2002-12-15
著者
-
Lee C.
Materials Processing Department Kimm
-
CHOI D.
Department of Mechanical Engineering, Korea Advanced Institute of Science and Technology
-
BRUCE D.
Advanced Steel Processing and Products Research Center, Colorado School of Mines
-
KIM S.
Materials Processing Department, KIMM
-
PARK S.
Automotive Steels Research Center
-
MATLOCK D.
Advanced Steel Processing and Products Research Center, Colorado School of Mines
-
SPEER J.
Advanced Steel Processing and Products Research Center, Colorado School of Mines
-
Speer J.
Advanced Steel Processing And Products Research Center Colorado School Of Mines
-
Matlock D.
Advanced Steel Processing And Products Research Center Colorado School Of Mines
-
Kim S.
Materials Processing Department Kimm
関連論文
- Two-dimensional viscous flow past a circular arc
- Deformation Behavior of Low Carbon TRIP Sheet Steels at High Strain Rates
- The Effects of Heating Rate on Austenite Grain Growth in a Ti-modified SAE 8620 Steel with Controlled Niobium Additions
- The Influence of Niobium Microalloying on Austenite Grain Coarsening Behavior of Ti-modified SAE 8620 Steel