Effect of Nb on the Proof Strength of Ferritic Stainless Steels at Elevated Temperatures

スポンサーリンク

概要

• 論文の詳細を見る

• The effect of Nb on the high temperature proof strength of 0.46% Nb-added ferritic stainless steel was studied from the viewpoints of solid solution strengthening, precipitation strengthening, and precipitation strengthening during tensile test and/or preceding hold time. The results obtained were as follows.(1) The increase in high temperature proof strength in Nb-added ferritic stainless steel is particularly remarkable at around 700°C in comparison with that in Ti-added steels.(2) After aging treatment for 2 h at 700°C, in addition to the approximately 0.14 % content of coarse Nb carbides and nitrides which had precipitated before this aging treatment, fine Fe2Nb Laves phase particles with a size of 0.02 μm precipitated out in an amount of approximately 0.3%, and virtually no solid solution Nb existed in the steel. The 700°C proof strength in this condition showed a value near the 700°C proof strength before the aging treatment, that is, when approximately 0.3% solid solution Nb was present.(3) When aging treatment is performed at 700°C for 2 h or more, virtually all the added Nb precipitates out. The coarsening of the Fe2Nb laves phase particles within the range of 0.02-0.05 μm during aging at 700°C greatly decreases the high temperature proof strength at 700°C.(4) Cold rolled steel sheets of Nb-added ferritic stainless steel are normally manufactured by annealing at a temperature of 900°C or higher in order to cause recrystallization. Accordingly, before measurement of the proof strength at 700°C, the steel contains a large quantity of solid solution Nb. The phenomenon of particularly high strength at 700°C is considered to be attributable to the precipitation of this solid solution Nb as a fine Fe2Nb Laves phase during the tensile test and/or preceding hold time.

• 社団法人 日本鉄鋼協会の論文
• 2002-08-15

著者

• MIYAZAKI Atsushi

  Mizusawa VERA Observatory, National Astronomical Observatory of Japan

• Takao Kenji

  Jfe Steel Corporation

• Miyazaki Atsushi

  Mizusawa Vera Observatory National Astronomical Observatory Of Japan

• Furukimi Osamu

  Technical Research Laboratories Kawasaki Steel Corporation

• Takao Kenji

  Technical Research Laboratories Kawasaki Steel Corporation

• MIYAZAKI Atsushi

  Technical Research Laboratories, Kawasaki Steel Corporation

関連論文

• Astrometry of H_2O Masers in Nearby Star-Forming Regions with VERA III : IRAS 22198+6336 in Lynds 1204G
• Aperture Synthesis Imaging of a High-Velocity Compact Cloud near the Galactic Center
• A Hyperenergetic CO Shell in the Galactic Center Molecular Cloud Complex
• A Molecular Cloud and an Expanding Cavity Adjacent to the Nonthermal Filaments of the Galactic Center Radio Arc
• Effect of Nb on the Proof Strength of Ferritic Stainless Steels at Elevated Temperatures
• High Nitrogen Stainless Steel as a Preferred Substratum for Bacteria and Other Microfouling Organisms
• A Galactic Center 50-kms^ Molecular Cloud with an Expanding Shell
• 熱延鋼板中の残留オーステナイトの歪安定性に及ぼす形態の影響
• Millimeter Light Curve with Abrupt Jump in Cyg X-3 2008 April-May Outburst
• Sagittarius A Molecular Cloud Complex in H^CO^+ and Thermal SiO Emission Lines
• Isolated Millimeter Flares of Cyg X-3

もっと見る 閉じる

スポンサーリンク