• An experimental study was carried out on the characterization of Ca in rare earth (R) alloy powders produced by the reduction-diffusion (R-D) method using metallic Ca as reductant. SmCo5, Sm2Fe17, Nd15Fe77B8, NdFe1.7Co0.3, Tb7Gd13Fe80 and MMNi4.2Co0.2Mn0.3Al0.3 (MM：mischmetal) alloy powders were prepared by the R-D method. The Ca content of the alloy powders by chemical analysis was from 0.03 wt. % to 0.45 wt. %. A SEM observation and an EPMA analysis of cross section of the alloy powders revealed that Ca was solute atom in several intermetallic compounds. The Ca content of intermetallic compounds increased as the rare earth content of intermetallic compounds increased. The Ca content of the alloy powders by chemical analysis and the sum of the Ca content of the intermetallic compounds by EPMA analysis were in agreement.

• 社団法人 資源・素材学会の論文
• 1999-07-25

著者

• 岡島 靖弘

  Central Research Laboratories Sumitomo Metal Mining Co. Ltd.

• 武谷 要

  住友金属鉱山(株)新居浜研究所

• 村上 旭

  住友金属鉱山新居浜研究所

• 青木 亜紀代

  住友金属鉱山中央研究所

• 武谷 要

  住友金属鉱山新居浜研究所

関連論文

• カルシウム還元法によるネオジム-鉄-ホウ素系合金粉末中の酸素およびカルシウムの低減と磁石適応性
• カルシウム還元法によるネオジム-鉄-ホウ素系合金粉末合成における添加元素の挙動
• 還元拡散法により製造されたSmFeN合金の磁気特性
• カルシウム還元法により作製された希土類合金粉末中の カルシウムの存在形態

スポンサーリンク