常圧焼結のよる窒化バナジウム基焼成物の作製とその性質
スポンサーリンク
概要
- 論文の詳細を見る
The effects of additives on the densification of vanadium nitride (VN) ceramics were prechecked by sintering. So we selected Y<SUB>2</SUB>O<SUB>3</SUB> as a sintering aid among several oxides (Al<SUB>2</SUB>O<SUB>3</SUB>, CaCO<SUB>3</SUB>, MgO, SiO<SUB>2</SUB>, TiO<SUB>2</SUB>, WO<SUB>3</SUB>, Y<SUB>2</SUB>O<SUB>3</SUB>, etc.). VN ceramics were prepared by pressureless sintering at 1800 to 2200°C for 2h in N<SUB>2</SUB> atmosphere. A sample added 5vol% Y<SUB>2</SUB>O<SUB>3</SUB> sintered at 2000°C gave the relative density (d<SUB>r</SUB>) of 96.2% and its Vickers hardness reached 16.2 GPa. As its spesific resistance is 1.2×10<SUP>-4</SUP> Ωcm at room temperature, it is possible to cut this by using of an arc cutting machine. The optical reflectivity of polished samples is light beige with metallic luster. It is concluded that polished samples (d<SUB>r</SUB>>95%) can be used for ornament.
- 社団法人 粉体粉末冶金協会の論文
- 2001-01-15
著者
関連論文
- ニッケルとシリコンを二重に添加したシリコンカーバイド焼結半導体の熱電特性
- 振動子2個用いて温度特性を改善した水晶発振回路
- 三次元炭素繊維で強化したフラン樹脂の加熱に伴う構造と曲げ強さの変化
- 硬化樹脂中に分散させた金属酸化物の炭化挙動
- 木材およびフルフリルアルコール樹脂含浸木材の炭化挙動と曲げ強度の密度依存性
- TiN基焼結体の色調に及ぼす添加物の効果
- 木炭の高温加熱処理に伴う曲げ強度と微細構造の変化
- 常圧焼結のよる窒化バナジウム基焼成物の作製とその性質