Ni_3Al金属間化合物の燃焼合成における緻密化要因の推定
スポンサーリンク
概要
- 論文の詳細を見る
To realize combustion synthesis process of intermetallic compound, a method of fabricating of full dense compound should be developed. In my previous paper, synthesis of Ni<SUB>3</SUB>Al intermetallic compound by pressureless combustion synthesis process was investigated. Consequently, it was found that density of the synthesized compound depended on initial powder particle size, and the nearly full dense product was obtained in case of using fine powders as initial substances. The densification might be caused by combustion temperature, compound formation ratio, quantities of liquid phases during the synthesis. However the details is not clear, to evolve the process, the cause of the densification and a course for producing the full dense compound should be established. In this paper, numerical analysis of the combustion synthesis of Ni<SUB>3</SUB>Al was performed as a continuation of the previous investigation, and the cause of densification was analyzed.<BR>A Ni/Al premixed compact during thermal explosion combustion synthesis was divided into infinite elements, numerical analysis model was derived under consideration of heat balance and material balance equations around the elements. The model was solved by I. A. D. method, the combustion synthesis behavior was analyzed.<BR>The compound formation behavior during the combustion synthesis was able to be simulated. The maximum combustion temperature or the ratio of compound formation at the each temperature during the synthesis did not depend on the powder particle sizes. However, the quantities of the liquid phases was greatly affected by the sizes, and it was guessed that the liquids is the cause of the densification. The quantities of the liquids were able to be increased by control of beginning temperature of the combustion, heat injection to the compact and enlargement of the compact size. Therefore, these countermeasures might be effective to synthesize the dense compound.
- 1996-10-15
著者
関連論文
- 金属粉末圧粉体の熱間電磁成形と燃焼合成法への応用の試み
- 電磁成形法による鉄圧粉体の衝撃圧縮
- 溶融AlへのTi線浸漬実験によるTiAl金属間化合物の燃焼合成過程の解析
- 燃焼合成法によるNi_3Al金属間化合物の合成とその条件
- Ni-Al系金属間化合物の燃焼合成時の燃焼波伝播の解析
- TiAl燃焼合成の生成相制御条件の解析
- Ni_3Al金属間化合物の燃焼合成における緻密化要因の推定
- Ni_3Al金属間化合物の燃焼合成時の燃焼温度, 化合物生成量ならびに発生液相量の解析
- B添加Ni_3Al金属間化合物の無加圧燃焼合成の試み
- Ni_3Al金属間化合物の無加圧燃焼合成の試み