Surface Crystallization of Lithium Niobate on a Silicate Glass (光機能材料<特集>)

スポンサーリンク

概要

• 論文の詳細を見る

• LiNbO<SUB>3</SUB> was crystallized with orientation along c-axis on the surface of a glass of the composition 35Li<SUB>2</SUB>O⋅0Nb<SUB>2</SUB>O<SUB>5</SUB>⋅35SiO<SUB>2</SUB> (in mol%). The dense surface layers were composed of fibrous-grain crystallites, and the thicknesses were controllable by changing heating temperature and time. Kinetic analysis indicated that crystallization of LiNbO<SUB>3</SUB> was diffusion controlled.

• 社団法人 粉体粉末冶金協会の論文
• 1995-01-15

著者

• Osaka Akiyoshi

  Dept. Of Appl. Chem. And Dept. Of Bioengineering Science Faculty Of Engineering Okayama University

• Ding Yong

  Dept. Of Appl. Chem. And Dept. Of Bioengineering Science Faculty Of Engineering Okayama University

• Miura Yoshinari

  Dept. Of Appl. Chem. And Dept. Of Bioengineering Science Faculty Of Engineering Okayama University

• Matsuoka Yoshihiko

  Materials Research Laboratory Hoya Corporation

• Matsuoka Yoshihiko

  Material Research Laboratory Hoya Corporation

• TORATONI Hisayoshi

  Materials Research Laboratory, Hoya Corporation

• Toratoni Hisayoshi

  Materials Research Laboratory Hoya Corporation

関連論文

• Refractive Index Change of Vanadyl Phthalocyanine Thin Film in Guided Wave Geometry (Special Section on Organic Functional Devices)
• Substrate Effect on Poling Process of Nonlinear Optical Polymer Films
• Surface Crystallization of Lithium Niobate on a Silicate Glass (光機能材料)

スポンサーリンク