Kinetic behavior of liquefaction of Japanese beech in subcritical phenol.
スポンサーリンク
概要
- 論文の詳細を見る
Non-catalytic liquefaction of Japanese beech (Fagus crenata) wood in subcritical phenol was investigated using a batch-type reaction vessel. After samples were treated at 160 °C/0.9 MPa-350 °C/4.2 MPa for 3-30 min, they were fractionated into a phenol-soluble portion and phenol-insoluble residues. These residues were then analyzed for their chemical composition. Based on the obtained data, the kinetics for liquefaction was modeled using first-order reaction rate law. Subsequently, the liquefaction rate constants of the major cell wall components including cellulose, hemicellulose, and lignin were determined. The different kinetic mechanisms were found to exist for lignin and cellulose at two different temperature ranges, lower 160-290 °C and higher 310-350 °C, whereas for hemicellulose, it was only liquefied in the lower temperature range. Thus, the liquefaction behaviors of these major cell wall components highlighted hemicellulose to be the most susceptible to liquefaction, followed by lignin and cellulose.
論文 | ランダム
- 材料の破壊に及す試驗片寸法の影響
- I 形梁の曲げ疲勞試驗
- 23. 急性心筋梗塞後に肺梗塞を発症した1例(第985回千葉医学会例会・第二内科例会)
- 22. 成人発症Still病と診断した1例(第985回千葉医学会例会・第二内科例会)
- 44. 糖尿病の経過中にネフローゼ症候群を呈した膜性腎症の1例(第968回千葉医学会例会・第二内科例会)