Characterization of wood-based molding bonded with citric acid
スポンサーリンク
概要
- 論文の詳細を見る
The wood-based moldings were fabricated by using only citric acid as an adhesive. Themechanical properties, water resistances, thermal properties and chemical structure were investigated. Wood powder obtained from Acacia mangium was mixed with citric acid under certain weight ratios (0-40 wt%), and each powder mixture was molded using two types of metal molds at 200 °C and 4MPa for 10 min. The modulus of rupture (MOR) and the modulus of elasticity (MOE) values of the wood-based molding containing 20wt% citric acid were 35.8 MPa and 5.4 GPa, respectively. The maximum impact strength was 0.94 kJ/m2 with the same citric acid content. The water resistance increased with increasing citric acid content, and thegood resistance to boiling water was also recognized. However, some elution of substances derived from citric acid was observed at high levels of citric acid, causing a decrease in the thermal properties. The ester linkages were detected by Fourier transform infrared spectroscopy (FT-IR), indicating that the citric acid reacted with the wood. Our results demonstrated that citric acid brings about good adhesiveness for fabricating the wood-based molding.
論文 | ランダム
- 233 ミニ・バスケットボール教室参加者のパーソナリティ(2) : ソシオメトリー構造や成員の地位とパーソナリティの追跡的検討
- Dance運動の筋電図学的研究 (5) : skipping stepについて
- Dance運動の筋電図学的研究 (5) : Hopping stepについて
- パケットマージ手法における出力パケットレートに基づくパケット結合方式の検討(基礎理論)
- JGN2を利用した東京工業大学-タイ王国チュラロンコン大学の高品質ネットワーク (海外との遠隔教育のハイビジョンの可能性について--JGN2回線を使用したタイ-日本間のH.264系HD IP伝送の報告)