Graphite Shell Film Formation Induced by Eduction Phenomenon of Ga Implanted by Focused Ion Beam
スポンサーリンク
概要
- 論文の詳細を見る
In this study, we used a transmission electron microscope (TEM) to evaluate the structure of the gallium (Ga) sphere formed on the tip of a diamond-like carbon (DLC) pillar fabricated by focused-ion-beam chemical vapor deposition (FIB-CVD). Until now, details of the phenomenon induced by Ga eduction were remained unclear. We found that a graphite shell was formed on the surface of the Ga sphere after annealing. In addition, we demonstrated that this graphite shell film could be separated from the Ga sphere by performing a second annealing treatment. In-situ observations of the formation of the graphite shell film were carried out using TEM to clarify the process by which it was separated from the Ga sphere. The thermal expansion of Ga led to the separation of the graphite shell film, and Ga was vaporized from within the Ga sphere. These results imply that Ga is able to catalyze for the graphitization of carbon. The development of carbon nanodevices can be expected by using this novel phenomenon induced by Ga.
- 2009-06-25
著者
-
ICHIHASHI Toshinari
NEC Corporation, Fundamental Research Laboratories
-
Ishihara Sunao
The University Of Tokyo
-
Kometani Reo
The University of Tokyo, 7-3-1 Hongo, Bunkyo-ku, Tokyo 113-8658, Japan
-
Ishihara Sunao
The University of Tokyo, 7-3-1 Hongo, Bunkyo-ku, Tokyo 113-8658, Japan
-
Ichihashi Toshinari
NEC Corporation, 34 Miyukigaoka, Tsukuba, Ibaraki 305-8501, Japan
-
Warisawa Shin'ichi
The University of Tokyo, 7-3-1 Hongo, Bunkyo-ku, Tokyo 113-8658, Japan
関連論文
- Graphite Shell Film Formation Induced by Eduction Phenomenon of Ga Implanted by Focused Ion Beam
- Modulated Structures in Superconductor Tl-Ba-Ca-Cu-O Oxides: Crystal Structure of Tl_2Ba_2CuO_ Phase : Electrical Properties of Condensed Matter
- Crystal Structure Variations due to Multiplicity in CuO_2-Ca-CuO_2 Slabs in Superconductive Tl-Ba-Ca-Cu-O Oxides : Electrical Properties of Condensed Matter
- Photomask Data Prioritization Based on VLSI Design Intent and Its Utilization for Mask Manufacturing
- Twinning of High-T_c Ba_2YCu_3O_ Oxides
- Structural Variations on Superconductor Tl-Ba-Ca-Cu-O Oxides : Electrical Properties of Condensed Matter
- Non-Core–Shell Nanostructure Deposition on Focused-Ion-Beam Chemical Vapor Deposition
- Three-Dimensional Nanostructure Fabrication by Controlling Downward Growth on Focused-Ion-Beam Chemical Vapor Deposition
- Evaluation of Thermal–Mechanical Vibration Amplitude and Mechanical Properties of Carbon Nanopillars Using Scanning Electron Microscopy
- Height Dependence of Young's Modulus for Carbon Nanopillars Grown by Focused-Ion-Beam-Induced Chemical Vapor Deposition