Experimental Investigation on Thermal Effects in Ultrasonic Joining of Thin Poly(ethylene terephthalate) Films Using Torsional Vibrations

概要

論文の詳細を見る
The authors previously determined that thermal effects are not a dominant factor in the ultrasonic joining of very low density polyethylene (VLDPE) films using torsional vibration. Now, to confirm that the plastic materials are not "melted" by mechanically generated heat in the joining, they have conducted joining experiments for thin poly(ethylene terephthalate) (PET) films. The temperature at the interface of two PET films of 0.1 mm thickness only increased to approximately 100 °C, and no trace of liquidation of the material was observed at the interface under a polarizing microscope. Investigation using a differential scanning calorimeter (DSC) revealed that the "melting point" of PET is about 260 °C, and an ultrasonically joined specimen showed no significant difference in thermal characteristics compared with an intact PET film. It was also determined that the PET films cannot be joined even after being pressed together for a period of 30 min or longer at approximately 150 °C. From the results obtained using the microscope and the DSC, the authors conclude that melting of the materials plays essentially no role in ultrasonic plastic joining.
Published by the Japan Society of Applied Physics through the Institute of Pure and Applied Physicsの論文
2009-11-25