Deep Level Transient Spectroscopy Analysis of an Anatase Epitaxial Film Grown by Metal Organic Chemical Vapor Deposition
スポンサーリンク
概要
- 論文の詳細を見る
The deep level transient spectroscopy (DLTS) study of anatase-type TiO2 material was performed for the first time. The anatase film was epitaxialy grown on a conductive Nb-doped single-crystalline SrTiO3 (100) substrate by metal organic chemical vapor deposition. The photoluminescence characteristics of this anatase film were identical to those in previous reports, where they were attributed to the radiative recombination of self-trapped excitons. According to the DLTS analysis, it was revealed that this anatase film had a characteristic deep level located at 0.96 eV below the bottom of the conduction band with large concentration ($6.5\times 10^{16}$/cm3) and capture cross section ($8.3\times 10^{-13}$ cm2). Since the capture cross section of this level appeared to be too large to be caused by point defects, the origin of this deep level was attributed to line defects such as dislocations.
- 2001-04-15
論文 | ランダム
- リアルな聴空間合成用耳栓型電気音響変換器の設計・製作
- 耳栓型電気音響変換器を用いたアクティブ・ノイズ制御の比較・検討
- 耳栓型電気音響変換器を用いたアクティブ・ノイズ制御
- 詩誌選評 ゴリラと耳栓
- エネルギー政策の転換は、脱官僚依存の政治と不可分 (特集 原発事故 政治とメディアの責任)