摩砕によるリン酸三コバルト八水和物のメカノケミカル変化
スポンサーリンク
概要
- 論文の詳細を見る
Mechanochemical phenomena of Co<SUB>3</SUB> (PO<SUB>4</SUB>) <SUB>2</SUB>.8H<SUB>2</SUB>O was studied by grinding.<BR>The crystal of Co<SUB>3</SUB> (PO<SUB>4</SUB>) <SUB>3</SUB>.8 H<SUB>2</SUB>O (plates, 3 × 10, am, pink) was converted easily into amorphous phase (bluish violet) as a result of mechanochemical dehydration.<BR>The ground materials were hydrated rapidly in water and recrystallized to fine grain Co<SUB>3</SUB> (PO<SUB>4</SUB>) <SUB>2</SUB>.8 H<SUB>2</SUB>O (particle size about O.2 μm).<BR>The temperatures of exothermic DTA peak for crystallization of ground materials were much varied by grind efficiency.<BR>The particle size and hue of pigments were improved by grinding and rehydration of Co<SUB>3</SUB> (PO<SUB>4</SUB>) 2.8 H<SUB>2</SUB>O.