アルカリ処理による木材の可塑化--応力緩和挙動に及ぼすアルカリの種類,濃度の影響
スポンサーリンク
概要
- 論文の詳細を見る
Stress relaxation behavior of wood treated with alkaline aqueous solution was investigated to clarify the efficiency of alkaline as a plasticizer of wood. Torsional stress relaxation of wood specimens treated with three kinds of alkali, namely, lithium hydroxide (LiOH), sodium hydroxide (NaOH) and potassium hydroxide (KOH), was measured in water at 30°C over a wide range of alkali concentration. Relaxation rigidity G<SUB>r</SUB> at 10<SUP>4</SUP> sec decreased remarkably in the concentration of 5-10% of the NaOH solution, while the corresponding decrease of G<SUB>r</SUB> treated with the KOH solution occurred at somewhat higher concentrations compared with those of NaOH. The coefficient of longitudinal shrinkage of the treated wood under water-saturated condition showed similar dependence on alkali concentration. Furthermore, a peak in relaxation spectrum of the treated wood shifted toward shoter time range above the concentration of 10% for NaOH and above 18% for KOH. It has been inferred from the results that slipping and loosing motions of the microfibrils in the wood cell being shrinked by the alkali treatment give rise to the stress relaxation phenomena. The wood plasticized by the present method has been found to be easily bent and molded, which indicates the versatility of the present method.
- 日本レオロジ-学会の論文
日本レオロジ-学会 | 論文
- ブロック共重合体の流動複屈折
- 低分子量ポリスチレン溶液の粘弾性
- 高分子混合系の粘弾性.ポリスチレン-ポリビニルメチルエ-テル混合物の溶液
- カルボキシル基を含有するコア・シェル粒子分散系の液構造に及ぼす溶媒組成の影響
- カルボキシル基を含有するコア・シェル粒子分散系における凝塑性発現