アルミニウム合金レーザ溶接部の疲労特性
スポンサーリンク
概要
- 論文の詳細を見る
Fatigue properties of CO2 laser welds in A5182P-O alloy were evaluated by the fatigue test, and the results were compared with those of the base metal and electron beam welds. The initiation and propagation of a fatigue crack during testing was investigated by observing the specimen surface through CCD video camera and by measuring strains with the gauges. Characteristics of fatigue crack surfaces were ana1yzed and confirmed by SEM observation of the specimens. Especially, porosity at the cross section of a specimen before the test was observed by X-ray CT method, and the influence of the porosity on the fatigue strength and cycles to fracture was evaluated in terms of the maximum porosity-occupation percentage per cross section. It was confirmed that the porosity in laser weld metals reduced the fatigue strength and cycles to fracture. It was also found that the maximum size and the percentage of the porosity should be decreased to the degrees of less than 0.5 mm and 1％, respectively, in order to produce the laser welds with good properties equivalent to those of the A5182 base alloy.
- 一般社団法人 軽金属溶接協会の論文
一般社団法人 軽金属溶接協会 | 論文
- AZ31マグネシウム合金の摩擦撹拌点接合時の塑性流動および継手強度に及ぼすツール形状の影響
- プラズマアークによるアルミニウム厚板のキーホール溶接の数値シミュレーション
- 5052Al及び6063Al合金のパルス通電接合部の熱処理による改善
- ブレージングシートの外部耐食性に及ぼす心材Cu量、ろう材Zn量および板厚の影響
- 半溶融状態のはんだを用いた超音波はんだ付によるアルミニウム継手の強度と耐食性