溶融Al-Si-Mg合金めっき鋼板のめっき組成と腐食挙動
スポンサーリンク
概要
- 論文の詳細を見る
This study was intended to investigate the effect of the amount of Mg and Si addition in the Al-Si coating in order to improve corrosion resistance of Aluminized steel sheets.A salt spray test using formed specimens proved that Al-8mass%Si-6mass%Mg-coated steel sheet having less cracks in the alloy layer after forming has the best corrosion resistance.This outdoor exposure test using unformed specimens for 10 years proved that corrosion weight loss of Al-8mass%Si-6mass%Mg-coated steel sheet was reduced to approximately 30% less than that of Aluminized steel sheets and approximately 70% less than that of 55% aluminum-zinc alloy-coated steel sheets; thereby, it was possible to confirm that Al-8mass%Si-6mass%Mg-coated steel sheet has favorable corrosion resistance under a long-term atmospheric environment.This is supported to be the protective effects caused by corrosion products mixed with Si and Mg, since the current value of the cathode polarization method of the specimen of Al-8mass%Si-6mass%Mg-coated steel sheet after the outdoor exposure test in an artificial rain solution were reduced by approximately 40% less than that of aluminized steel sheet.
- 日本鉄鋼協会の論文
日本鉄鋼協会 | 論文
- 製鋼における自動化技術計測技術の進歩 (21世紀に向けて--鉄鋼技術10年の軌跡) -- (製鋼)
- サンプル値制御系入門 : サンプル点間応答を考慮した設計
- 金属間化合物析出強化型9Cr-7Mo鋼の高温特性に及ぼすNiの影響
- 入門講座 材料の変形と破壊の熱力学
- 討 20 複合組織型鋼板の引張特性プレス成形時の形状性および深絞り成形後の靱性と組織との関係(IV 冷延高張力鋼板, 第 100 回講演大会討論会講演)