Zirconia ceramics, their contrast ratio and grain size depending on sintering parameters
スポンサーリンク
概要
- 論文の詳細を見る
This study investigated the contrast ratio and grain size depending on sintering parameters of twelve different zirconia materials and compared with glass-ceramic (N=156, n=12 per group). Contrast ratio of all ceramics was measured using a spectrophotometer according to ISO 2471: 2008. Grain sizes of zirconia were determined by SEM. Data was analyzed using one-way ANOVA followed by post-hoc Scheffé-test, Kruskal-Wallis-H-test and Spearman correlation (p<0.05). The area under the sintering curve up 25°C (AUC25) and 1200°C (AUC1200) of zirconia was calculated. Glass-ceramic showed significantly lowest contrast ratio compared to zirconia. Final sintering temperature and AUC1200 influenced contrast ratio. Grain size was affected by final sintering temperature, sintering duration and AUC. Contrast ratio and grain size showed an association.
- 日本歯科理工学会の論文
日本歯科理工学会 | 論文
- A-33 レイヤリングテクニックとプレスオンテクニックにより製作したジルコニアクラウン(セラミックス,一般講演(口頭発表),第54回日本歯科理工学会学術講演会)
- B-4 IPS Empress 2コア材の繰り返し焼成が接着強さに与える影響(接着2, 第49回日本歯科理工学会学術講演会)
- IPS Empress 2ガラスセラミックスの最適な表面処理条件 : 第1報 各種酸処理が曲げ強さに与える影響(臨床応用, 平成17年度秋期 (長崎) 第46回日本歯科理工学会学術講演会)
- P-95 骨芽細胞様細胞によるジルコニアとチタンの生体適合性の比較評価(生体用セラミックス2,一般講演(ポスター発表),第54回日本歯科理工学会学術講演会)
- A-13 シリコン種含有ポリ乳酸系ハイブリッド膜の生体適合性評価(生体反応2,一般講演(口頭発表),第53回日本歯科理工学会学術講演会)