A new method for fabricating zirconia copings using a Nd:YVO4 nanosecond laser
スポンサーリンク
概要
- 論文の詳細を見る
The purpose of this work was to fabricate zirconia copings from fully sintered Y-TZP blocks using a Nd:YVO4 nanosecond laser in order to avoid complicated procedures using conventional CAD/CAM systems. To determine the most appropriate power level of a Nd:YVO4 laser, cuboid fully sintered Y-TZP specimens were irradiated at six different average power levels. One-way ANOVAs for the average surface roughness and laser machining depth revealed that an average power level of 7.5 W generated a smooth machined surface with high machining efficiency. Y-TZP copings were then machined using the proposed method with the most appropriate power level. As the number of machining iterations increased, the convergence angles decreased significantly (p<0.01). The accuracy of the machined copings was judged to be good based on 3D measurements and traditional metal die methods. The proposed method using the nanosecond laser was demonstrated to be useful for fabricating copings from fully sintered Y-TZP.
- 日本歯科理工学会の論文
日本歯科理工学会 | 論文
- A-33 レイヤリングテクニックとプレスオンテクニックにより製作したジルコニアクラウン(セラミックス,一般講演(口頭発表),第54回日本歯科理工学会学術講演会)
- B-4 IPS Empress 2コア材の繰り返し焼成が接着強さに与える影響(接着2, 第49回日本歯科理工学会学術講演会)
- IPS Empress 2ガラスセラミックスの最適な表面処理条件 : 第1報 各種酸処理が曲げ強さに与える影響(臨床応用, 平成17年度秋期 (長崎) 第46回日本歯科理工学会学術講演会)
- P-95 骨芽細胞様細胞によるジルコニアとチタンの生体適合性の比較評価(生体用セラミックス2,一般講演(ポスター発表),第54回日本歯科理工学会学術講演会)
- A-13 シリコン種含有ポリ乳酸系ハイブリッド膜の生体適合性評価(生体反応2,一般講演(口頭発表),第53回日本歯科理工学会学術講演会)