A material with comparable tensile properties to conventional TiAl intermetallic compounds was fabricated by compression shearing at room temperature. Pure Ti and pure Al powders were mixed by ball milling. Mixing time was varied between 10 and 540 min. The tensile properties of the formed samples were measured. The results reveal that the Ti/Al thin plates were not mechanically alloyed. Rather, they consisted of separate Ti and Al phases. Tensile strength increased from 100 to 500 MPa when the milling time was increased from 10 to 540 min. Thin Ti/Al plates that were milled for 360 and 540 min were found to have similar tensile strength to conventional TiAl intermetallic compounds.
- The Japan Society for Technology of Plasticityの論文
The Japan Society for Technology of Plasticity | 論文
- Hot Spline Forming of Ultra High Strength Steel Gear DrumUsing Resistance Heating
- 表面品質向上に向けた圧延油の最前線
- 鍛造加工におけるドライ・セミドライ化
- Effects of Friction Coefficient and Die Pressure in Drawingon Surface Gloss of Ni-plated Steel Wire:— Effects of Drawing Conditions on Surface Gloss of Ni-plated Steel Wire (2) —
- 金型材料の熱伝導率が熱間鍛造特性へ及ぼす影響