ＭＩ磁界差センサによる構造鋼材の塑性変形評価
スポンサーリンク
概要
- 論文の詳細を見る
This paper reports a nondestructive evaluation (NDE) method using amorphous wire MI sensors to determine the plastic deformation of steel samples. The distributions of the flux density on the surfaces of steel samples were measured. The flux density at the Lüders band was found to be clearly higher than that in non-deformed parts of the sample. The profile of contour lines for flux intensity is similar to the profile of Lüders lines. The magnetic signal from the Lüders band can be detected up to d (lift-off) = 50 mm, even for a sample covered with coating. The flux distribution for longitudinal direction of the sample was calculated, on the assumption that the magnetic poles are localized in the Lüders bands. The calculation results agree with the experimental data.
- 社団法人 日本磁気学会の論文
社団法人 日本磁気学会 | 論文
- Analysis of eddy-currents interaction with a flaw in a conductive plate
- Performance of U-shaped Core Orthogonal Fluxgate Magnetometer
- MFM Images and Micromagnetic Simulation of Submicron-Sized Single-Crystal Co particles
- Investigation of Magnetic Anisotropy for α-Fe/Nd2Fe14B Composition Alloy as Exchange-Spring Magnets Prepared Using Hot-Upsetting Technique
- Effect of Annealing Temperature on the Switching Field of Magnetic Force Microscope Tip Coated with FePd-Alloy Thin Film