表面処理を行ったＡｌ５０８３‐Ｈ１３１合金の高速衝突特性
スポンサーリンク
概要
- 論文の詳細を見る
Superior amore materials, generally, have high hardness and tension. This study investigated the fracture behaviors and the penetration resistance performances of cold-rolled Al alloy laminates, anodizing Al alloy laminates, and coldrolling and anodizing to material hardness and tension. To do this we conducted ballistic testing. We measured ballistic resistance of these materials at the protection ballistic limit, BL V50, under the conditions that a 5.56mm ball projectile had a velocity of 50% probability for complete and incomplete penetration; the test specimens were set at 0° obliquity at room temperature. The penetration resistance value was decided based on the measuring method "protection ballistic limit (V50)" by MIL-STD-662E. A high speed camera allowed us to capture and analyze the dynamic perforation phenomena of the test materials.
- 一般社団法人 日本非破壊検査協会の論文
一般社団法人 日本非破壊検査協会 | 論文
- フーリエ級数係数を用いたパッシブ赤外線サーモグラフィによるコンクリートのはく離深さ評価
- 複数探触子を用いたTOFD法によるきずの位置と寸法の同定法
- 厚肉材に渦電流探傷法を適用するための新しい励磁手法の提唱
- 鋼板厚さ測定におけるパルス渦電流試験の解析と実験からの検討
- ログアンプとリニアアンプの併用による超音波探傷試験