Al テープ上への超伝導 MgB2 薄膜の作製と特性評価
スポンサーリンク
概要
- 論文の詳細を見る
We prepared MgB2 thin films on non-textured aluminum (Al) tapes using an electron-beam evaporation technique. Single phases of MgB2 films with a c-axis and without biaxial crystal orientation were obtained with the critical temperatures (Tc) of 19-29.8 K, corresponding to the substrate temperature of 200-280°C. The magnetic field dependences of the critical current density (Jc) were measured at 4.2, 10 and 20 K in the field of 0-12 T applied parallel and perpendicular to the film surface. The Jc at 10 and 20 K in the self field were 3.1×106 A/cm2 and 1.2×106 A/cm2, respectively. Jc at 4.2 K exceeded 106 A/cm2 in the parallel and perpendicular fields of between 0 and 10 T. These results suggest that a MgB2 coated conductor may be one of the most promising candidates for practical MgB2 superconducting wires.
- 公益社団法人 低温工学・超電導学会 (旧 社団法人 低温工学協会)の論文
公益社団法人 低温工学・超電導学会 (旧 社団法人 低温工学協会) | 論文
- Test Results of the SMES Model Coil. Cool-down and Thermal Characteristics.:Cool-down and Thermal Characteristics
- Crystal Growth of Y Based Superconductors on Solidification Processing.
- Refrigeration of pressurized He II using a 3He circulation system. (II). Behavior of the system during the initial cooling and after a pulsed heat generation.:Behavior of the System during the Initial Cooling and after a Pulsed Heat Generation
- Quench simulation analysis of a superconducting coil. II. Simulation.:II. Simulation
- タイトル無し