溶湯発泡法で作製されたポーラス Zn-22Al 超塑性合金のセル形態に及ぼす発泡条件の影響

概要

論文の詳細を見る
Closed-cell superplastic Zn-22Al eutectoid alloy foams were manufactured through the melt foaming process using titanium hydride powder as a foaming agent. Foaming tests were carried out under different foaming temperatures, times and additive amounts of foaming agent. Maximum porosity of 75% and small pore diameter were obtained during the temperature range of semi-solid condition from 738-753 K. This is because of increased melt viscosity. Though the small amount of the foaming agent is effective to decrease the pore diameter, the porosity becomes low. Cell morphology of the present Zn-22Al alloy foam is identical to conventional aluminum foams. Semi-solid condition of Zn-22Al foam has an advantage over increasing melt viscosity on manufacturing of metal foam.
日本金属学会 ; 1937-の論文