ＡＺ３１Ｂマグネシウム合金の半溶融状態での固相の球状化に及ぼす熱処理と加工の影響
スポンサーリンク
概要
- 論文の詳細を見る
The structural changes of AZ31B in the semisolid state are clarified in terms of the responses of AZ31B to a certain heat treatment temperature, holding time, heating rate and deformation rate. Two types of test piece are adopted, namely, the heat-extruded material without predeformation and that with predeformation, resulting in a 30% height reduction at 573 K(300°C). The following are the main results. (1) The heat-extruded material without predeformation only exhibits grain growth after a long holding time. (2) The heat-extruded material with 30% predeformation shows an almost perfectly spheroidized structure in the semisolid state at a temperature of 883K, heating rate of 2 K•s-1 and holding time of 120 s. (3) The heating rate markedly affects the spheroidizing rate of grains. In the case of the heating rate is larger than the diffusion rate at a semisolid temperature, it is difficult to obtain the spheroidized semisolid structure.
- The Japan Institute of Metals and Materialsの論文
The Japan Institute of Metals and Materials | 論文
- Control of Ferromagnetism in Magnetic Semiconductors and Application for Spin-polarized Electron Source
- 超高純度金属の実用化への道
- 非極性 GaN 層中の微結晶粒の効率的な検出と今後の展望
- Recycling Technology for Platinum Group Metals by Using Perovskite-type Oxides
- Specimen Preparation Methods with FIB for In-Situ TEM Observations in Materials Science—TEM Specimen Preparation by FIB with Glass Manipulator—