Corrosion Properties of Ca Based Bulk Metallic Glasses
スポンサーリンク
概要
- 論文の詳細を見る
The corrosion properties of ternary (Ca<SUB>65</SUB>Mg<SUB>15</SUB>Zn<SUB>20</SUB> and Ca<SUB>50</SUB>Mg<SUB>20</SUB>Cu<SUB>30</SUB>), quaternary (Ca<SUB>55</SUB>Mg<SUB>18</SUB>Zn<SUB>11</SUB>Cu<SUB>16</SUB>), and quinternary (Ca<SUB>55</SUB>Mg<SUB>15</SUB>Al<SUB>10</SUB>Zn<SUB>15</SUB>Cu<SUB>5</SUB>) amorphous alloys were evaluated using static aqueous submersion at room temperature. Ca-Mg-Zn and Ca-Mg-Cu alloy systems experienced destructive corrosion reactions. Ca-Mg-Zn-Cu and Ca-Mg-Zn-Cu-Al based amorphous alloys demonstrated positive corrosion properties, forming corrosion films up to 23 μm thick in the quaternary alloy and 11 μm thick in the quinternary composition. Corrosion products were evaluated using X-ray diffraction (XRD), X-ray Fluorescence (XRF), Scanning Electron Microscopy (SEM), and Energy Dispersive Spectroscopy (EDS).
- Japan Institute of Metalsの論文
Japan Institute of Metals | 論文
- Isothermal Martensitic Transformation in Sensitized SUS304 Austenitic Stainless Steel at Cryogenic Temperature
- Effect of Magnetic Field on Microstructure Evolution during Disorder-Order Transformation in an Fe-Pd Alloy
- Time-Temperature-Transformation Diagram of Successive γ→ε'→α' Martensitic Transformation in SUS304L Stainless Steel
- Effects of Magnetic Field and Deformation on Isothermal Martensitic Transformation in SUS304 and SUS304L Steels
- Effect of Magnetic Field on γ-α Transformation in Fe-Rh Alloys