ショットピーニング後に人工腐食ピット加工を施した懸架ばね用鋼の疲労特性に及ぼす水素の影響
スポンサーリンク
概要
- 論文の詳細を見る
In order to reduce the weight of the suspension springs by increasing the steel strength, it is necessary to improve the corrosion fatigue property. However, the dominant factor governing the corrosion fatigue property of the suspension spring has not been satisfactorily revealed yet. Therefore, the investigation into elucidating the mechanism has been carried out to independently evaluate the influences of corrosion pits, shot peening, hydrogen, prior-austenite grain size, and so forth on the corrosion fatigue property. In this study, the influence of hydrogen on rotary bending fatigue test was investigated using specimens with artificial corrosion pits after shot peening. The dominant factors governing the corrosion fatigue property of the suspension spring were discussed based on the result of the present study in conjunction with the results of the previous study on the influences of shot peening and corrosion pit depth. The conclusions obtained were as follows: (1) In the case of the specimen without corrosion pit or with only shallow corrosion pits having still large compressive residual stress at the bottom of the pits, the fatigue property was fairly good but declined with the increment of charged hydrogen due to the diffusible hydrogen. On the other hand, in the case of the specimen with deep corrosion pits having only small compressive residual stress, the fatigue property was poor regardless of the charged hydrogen content. We inferred from this result that the deep corrosion pit releases the compressive residual stress at the bottom of pits. (2) The effect of prior-austenite grain size on fatigue properties of hydrogen charged specimens turned out to be almost negligible.
- 日本ばね学会の論文
日本ばね学会 | 論文
- 形状記憶合金への超音波ショットピーニングの影響
- ショットピーニングにより無害化可能な表面欠陥寸法の破壊力学的評価
- ショットピーニング処理後に人工ピットを導入したばね鋼の疲労特性
- ばね鋼の切欠き疲労強度予測
- 鉄粉層内蔵ばね型アクチュエータを用いたリニア平面位置制御機構の開発