Development of High Fatigue Strength Fine Grained Stainless Steel and Suitable Fatigue Test for Cylinder Head Gasket
スポンサーリンク
概要
- 論文の詳細を見る
High fatigue strength stainless steel was developed for cylinder head gasket. Bead is press formed on the stainless steel gasket to prevent the leak of combustion gases and cooling water. However, fatigue failure is initiated from micro crack on the bead foot induced by press forming. On the developed steel, the micro crack was suppressed by refining the grain size to 1.5∼2.0μm. In addition, suitable fatigue test method for gasket was invented. It was difficult to properly evaluate the fatigue strength of stainless steel for gasket by traditional fatigue test because the test piece had neither bead nor the micro crack on the bead foot. On this invented test, cyclic compressive load is applied to test piece with bead. It was clarified that the developed steel exhibited higher fatigue strength than the conventional steel.
- 日本ばね学会の論文
日本ばね学会 | 論文
- 形状記憶合金への超音波ショットピーニングの影響
- ショットピーニングにより無害化可能な表面欠陥寸法の破壊力学的評価
- ショットピーニング処理後に人工ピットを導入したばね鋼の疲労特性
- ばね鋼の切欠き疲労強度予測
- 鉄粉層内蔵ばね型アクチュエータを用いたリニア平面位置制御機構の開発