強加工された窒化ケイ素／炭化ケイ素複合材のき裂治癒による強度回復
スポンサーリンク
概要
- 論文の詳細を見る
The self crack-healing behavior of the heavily machined cracks in Si<SUB>3</SUB>N<SUB>4</SUB>/ 20 wt% SiC composite was investigate. The machined cracks were introduced in the center of specimens during making a semicircular groove by the diamond ball-drill. The machined specimens were crack-healed in various temperatures and time in air. The optimized crack-healing condition was found to be temperature of 1400℃ and time of 10 h in air. The specimen crack-healed in this condition showed the almost same strength as the smooth specimen healed. Moreover, the fracture strengths and fatigue strength of machined specimen healed at optimized condition were systematically investigated at high-temperature. The high-temperature strengths and cyclic fatigue strength of the machined specimen healed showed 700 MPa up to 1400℃, 550 MPa at 1300℃, respectively. These results demonstrate that the crack-healing could be very useful method to reduce machining cost and to increase reliability on Si<SUB>3</SUB>N<SUB>4</SUB>/ SiC composite ceramic.
- 日本ばね学会の論文
日本ばね学会 | 論文
- 形状記憶合金への超音波ショットピーニングの影響
- ショットピーニングにより無害化可能な表面欠陥寸法の破壊力学的評価
- ショットピーニング処理後に人工ピットを導入したばね鋼の疲労特性
- ばね鋼の切欠き疲労強度予測
- 鉄粉層内蔵ばね型アクチュエータを用いたリニア平面位置制御機構の開発