強磁性材を含むカプセル化分散染料のポリエステルフィルムへの拡散
スポンサーリンク
概要
- 論文の詳細を見る
Sublimation/diffusion behavior of a microencapsuled dye (1-aminoanthraquinone(AAQ), C.I. Solvent Blue 35 and C.I. Disperse Red 50) into poly (ethylene terephthalate)(PET) film was evaluated applying the film roll method. Eight kinds of microcapsules (smaller than 15 μm in diameter) containing both dyestuff and ferromagnetic substance or only the dyestuff were prepared by using acrylate resin as capsul material. Fickian diffusion profiles of three kinds of dye were obtained both from free state and from microcapsules in the temperature range from 170 to 200°C. Hence, the diffusion coefficients <I>D</I> could be calculated using the equation (ln <I>C</I>=A−(χ<SUP>2</SUP>/4<I>t</I>)·1/<I>D</I>), where <I>C</I> is the concentration at distance χ from surface after time t and A is a constant. From the temperature dependence of the <I>D</I>, the activation energy (Δ<I>E</I>) for diffusion was calculated. Δ<I>E</I> for diffusion from microcapsules was a little larger than from free state. It was also found that there is no influence of ferromagnetic substance on diffusion. This fact indicates that the capsule wall affected as "a very low diffusion barrier".
- 社団法人 繊維学会の論文
社団法人 繊維学会 | 論文
- 昆虫生産物を用いた新素材開発研究の現状
- 学会発表にみる研究開発の動機付け
- 酵素を用いる糖質マクロモノマーの合成
- ブロック化イソシアネートオリゴマーによるセルロース及びポリエステルの表面改質
- Thermoplastic Polyesters of 2-Pyrone-4,6-Dicarboxylic Acid (PDC) Obtained from a Metabolic Intermediate of Lignin