Paramagnetic Resonance Absorption in Annealing Process of Radiation-Damaged Graphite
スポンサーリンク
概要
- 論文の詳細を見る
An ESR study has been made of the isothermal annealing of radiation damage in a reactor-grade polycrystalline graphite after fast neutron bombardment at room temperature to total dose of 5.8×10<SUP>20</SUP> nvt. The absorption found for the specimens annealed below 950°C is concluded to be due to the unpaired electrons which as pointed out by Mrozowski are localized to the radiation-induced defects. On the other hand, for those annealed above 1450°C the Pauli-McClure type paramagnetism due to conduction carriers takes main part in ESR, while the localized spin centers still participate to some extent. In the annealing range between 1000°C and 1400°C no absorption signals have been observed, which is likely due not to the complete extinction of spin species but to the extreme broadening of line originating from some structural reasons.
- 炭素材料学会の論文
炭素材料学会 | 論文
- 「Carbon 2005」レポート
- 炭素複合ボードの建築内装材としての実用性能とその応用
- 炭素複合ボードの酸化ホウ素処理による難燃化機構
- ホウ酸トリエチルを添加したフェノール樹脂-オルトケイ酸テトラエチル複合体からの炭化ケイ素の生成機構
- 熱処理により鉄原子が表面に結合した炭素材料の燃料電池正極触媒としての可能性